The invention discloses a method for preparing hollow three-dimensional crimp polyphenylene sulfide staple fiber, using two kinds of components, the melt index is 50 ~ 150g/10min linear polyphenylene sulfide, wherein the first component and the second component of the melt index difference of 10 ~ 50g/10min; in 300 ~ 350 DEG C melting spinning; used spinneret spinneret for two concentric annular ring, and the ring is provided with two ring ring gap; hairdryer blowing cooling velocity is 0.8 ~ 1.5m/s, the blowing angle of the upper level wind ring blowing down 10 to 20 degrees; the spinning speed is 800 ~ 1000m/ min, after 2 ~ 5 times of stretching and cutting and 180 to 220 DEG C high temperature molding prepared hollow polyphenylene sulfide staple fiber. The product of the invention has the advantages of good operability, good mechanical performance, high hollowness, etc., and is especially suitable for being used in high temperature protective clothing, heat insulation nonwoven cloth and so on.
【技术实现步骤摘要】
本专利技术涉及一种中空聚苯硫醚短纤维的制备方法，特别是，属于高性能纤维
技术介绍
聚苯硫醚(PPQ树脂是分子主链中带有苯硫基的热塑性树脂，由PPS树脂制成的 PPS纤维是一种新型的高性能纤维，具有优良的耐热性能、耐化学性、阻燃性能及良好的力学性能、尺寸稳定性及纺织加工性。因此，PPS纤维在产业和纺织服装领域得到了广泛的应用。目前开发的PPS纤维，主要以普通圆形短纤维为主，如公开号CN1603477公开的是 “一种线性高分子量聚苯硫醚纤维熔融纺丝、拉伸热定型方法”，该方法生产出的圆形截面短纤维，具有断裂强度高、断裂伸长低和热稳定性高等特点。公开号CN101275309公开的是一种“聚苯硫醚短纤维及其制造方法”，该专利技术的聚苯硫醚短纤维，拉伸强度达5. OCN/dtex 以上，此类产品主要用于生产高温除尘的过滤袋，以进一步延长使用寿命。常规圆形截面的聚苯硫醚纤维与同规格的中空的聚苯硫醚纤维相比，其导湿性、 透气性、保温性和隔热效果较差，当作为耐高温防护服、隔热非织造布时，其缺点尤为明显。作为一般熔融纺丝纺制中空纤维的方法，已有比较成熟的技术，如聚酯(PE...
【技术保护点】
１．一种中空三维卷曲聚苯硫醚短纤维的制备方法，其特征在于：采用二种组分，其熔融指数为５０～１５０ｇ／１０ｍｉｎ的线型聚苯硫醚，其中第一组分与第二组分的熔融指数差为１０～５０ｇ／１０ｍｉｎ；通过双螺杆复合纺丝装置，在３００～３５０℃的温度下熔融纺丝；所用喷丝板的喷丝孔为二个同心圆组成的圆环，且圆环上开有二个缺口；环吹风筒的环吹风冷却风速为０．８～１．５ｍ／ｓ，环吹风筒上部的吹风角度为水平向下１０～２０°；纺丝速度为８００～１０００ｍ／ｍｉｎ ，经２～５倍的拉伸、切断和１８０～２２０℃的高温热定型制得中空聚苯硫醚短纤维。
【技术特征摘要】
【专利技术属性】
技术研发人员：王秀华，沈国锋，詹勇，万继宪，马艳丽，
申请(专利权)人：浙江理工大学，浙江东华纤维制造有限公司，
类型：发明
国别省市：86