The invention relates to a natural macromolecule medical biological material technology, and discloses an tussah silk fibroin film and a preparation method thereof. The tussah silk fibroin solution adding non-toxic diol as crosslinking agent, the injection mold, forming the tussah silk fibroin film after drying. By weight, it contains 40 to 90% of tussah fibroin, and the protein dissolution rate of the membrane is less than 3% in 37 hours in water for 24 hours. The tensile fracture strength is greater than 20Mpa and the elongation at break is greater than 20%. Due to the absence of additional chemical cross-linking agents or the use of chemical denaturant in the preparation process, the biocompatibility of tussah fibroin will not be reduced and the biocompatibility of tussah fibroin will be maintained. This is difficult to dissolve in the tussah silk fibroin membrane can be used for artificial cornea, dura, esophagus, heart valves, and vascular wound covering material, as well as the temporary coverage, tissue isolation, drug controlled release materials etc..
【技术实现步骤摘要】
本专利技术涉及一种天然高分子医用生物材料技术，特别涉及一种柞蚕丝素蛋白膜及 其制备方法，所制备的材料可应用于人造角膜、硬脑膜、食道、心脏瓣膜、血管和创面覆盖材料等。
技术介绍
柞蚕是野蚕中的一种，以柞叶为食。柞蚕丝是以柞蚕茧为原料缫制而成的天然蚕 丝纤维。我国年产柞蚕茧3 4万吨，占世界柞蚕茧总产量的90%以上，这是世界稀有、我 国特有的宝贵资源，但目前柞蚕丝主要用作普通的纺织原料，所体现出的经济价值十分有 限。柞蚕丝素的蛋白质组成中以甘氨酸、丙氨酸和丝氨酸为主，具有良好的生物相容性，其 本身及其降解产物对细胞和机体无毒，不会或较少引起炎症和免疫排斥反应，其蛋白质分 子中含有的RGD三肽序列。RGD序列作为细胞膜整合素受体与细胞外配体相结合的识别位 点，介导细胞与细胞外基质及细胞之间的相互作用，能够促进支架对细胞的戮附，使得细胞 在柞蚕丝素膜上的附着率和增殖率远优于桑蚕丝素膜上的附着率和增殖率，因此柞蚕丝素 蛋白材料可视为新型用于人体的理想生物和医学材料。柞蚕丝是一种纤维状的材料，将柞蚕丝素蛋白制成膜状材料，一般是先将柞蚕丝 脱胶后制备成柞蚕丝素蛋白水溶液，再采...
【技术保护点】
１． 一种柞蚕丝素蛋白膜，其特征在于：按重量计，它含有柞蚕丝素蛋白质４０～９０％，其余为二元醇；它在３７℃的水中２４小时的蛋白溶失率小于３％，拉伸断裂强度大于２０Ｍｐａ，拉伸断裂伸长率大于２０％；所述的二元醇为乙二醇、１，３－丙二醇、２，３－丙二醇、１，４－丁二醇、１，２－丁二醇、１，３－丁二醇、２，３－丁二醇、一缩二乙二醇和二缩三乙二醇中的一种，或它们的任意组合。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。