Holmium ytterbium Co doped potassium lithium niobate single crystal and a preparation method thereof, which relates to the potassium lithium niobate crystal and its preparation method. The invention is to solve the technical problems in there is no conversion performance for lithium niobate substrate material on the frequency. The invention of the double doped holmium ytterbium doped lithium potassium niobate is made of ytterbium oxide, holmium oxide, niobium oxide and lithium carbonate and potassium carbonate; methods: weigh ytterbium oxide, holmium oxide, niobium oxide and lithium carbonate and potassium carbonate and mixed evenly, and then placed in the crucible after grinding, in the crystal growth furnace the sintered KLN polycrystalline, with gradual cooling method, namely holmium ytterbium Co doped potassium lithium niobate crystal. The single crystal of the invention generates 545nm green light and 650nm red light under the excitation of an 975nm laser, and can be used in the fields of frequency conversion, short wave length, all solid state laser, solar cells, color display and biological identification, and other fields.
【技术实现步骤摘要】
本专利技术涉及铌酸钾锂单晶及其制备方法。
技术介绍
上转换荧光材料由于可以将泵浦能量由近红外光谱区域传递到可见光或者是紫 外光谱区域而受到了普遍的关注。铌酸钾锂(K3_yLi2_x+yNb5+x015+2x)因为具有非常优秀的热 电、铁电、压电和非线性光学效应，是一种具有极高潜在应用价值的材料。但是目前对铌酸 钾锂晶体或掺杂的铌酸钾锂晶体(如双掺铈锰铌酸钾锂晶体)的研究都是围绕晶体的非线 性光学和铁电效应方面的性能进行的，目前还没有以铌酸钾锂为基质的具有频率上转换性 能的材料的报道。
技术实现思路
本专利技术是要解决目前尚没有以铌酸钾锂为基质的频率上转换性能的材料的技术 问题，而提供。本专利技术的钬镱双掺铌酸钾锂单晶是由氧化镱、氧化钬、氧化铌、碳酸锂和碳酸 钾制成的，其中氧化镱与氧化钬的摩尔比为1 0.5 8，氧化镱与氧化铌的摩尔比为 1 1263 1似8，氧化镱与碳酸锂的摩尔比为1 571 637，氧化镱与碳酸钾的摩尔比为 1 857 957。本专利技术的钬镱双掺铌酸钾锂单晶的制备方法按以下步骤进行一、称取氧化镱、氧 化钬、氧化铌、碳酸锂和碳酸钾并混合...
【技术保护点】
１．钬镱双掺铌酸钾锂单晶，其特征在于钬镱双掺铌酸钾锂单晶是由氧化镱、氧化钬、氧化铌、碳酸锂和碳酸钾制成的，其中氧化镱与氧化钬的摩尔比为１∶０．５～８，氧化镱与氧化铌的摩尔比为１∶１２６３～１４２８，氧化镱与碳酸锂的摩尔比为１∶５７１～６３７，氧化镱与碳酸钾的摩尔比为１∶８５７～９５７。
【技术特征摘要】
【专利技术属性】
技术研发人员：周忠祥，李磊，封雷，宫德维，
申请(专利权)人：哈尔滨工业大学，
类型：发明
国别省市：93