The invention discloses a storage plant oil based polyurethane wood adhesive is composed of the following 20% to 50% weight percent of vegetable oil polyol, isocyanate, 25% ~ 45% ~ 0.1% and 5% ~ 0.01% catalyst 35% solvent made of raw materials, in line with the current new material, green environmental protection and low carbon material has a good development trend. Storage, good adhesion, good water resistance and storage period is long, and it can be cured at room temperature, can be used in the wood adhesive. The invention also discloses a preparation method of a storable vegetable oil based polyurethane wood adhesive, which has the advantages of simple steps, low requirement of technological conditions, high economic benefit and favorable industrial production.
【技术实现步骤摘要】
本专利技术涉及胶黏剂领域，特别涉及一种可储存的植物油基聚氨酯木材胶黏剂、制 备方法及应用。
技术介绍
植物油基聚氨酯胶黏剂是近年来一直在研究的一种新型胶黏剂，它是以可再生的 植物油多元醇为原料合成的胶黏剂，具有良好初粘性、无甲醛释放、耐水性好、耐老化性能 好、胶接强度高等优点。植物油基聚氨酯胶黏剂的粘接效果可与相应的石油基材料媲美，同 时，具有较好的环境效益、经济效益及社会效益。植物油基聚氨酯胶黏剂是异氰酸酯与植物油多元醇共聚产物，其分子链中含有活 泼的-NCO基团及-NHCOO-基团，易与被粘结材料中含有活泼氢的物质发生反应，制备成具 有良好胶接性能的材料。由于所选取的植物油多元醇及异氰酸酯性质不同，如羟值不同、分 子量不同、化学基团种类不同、异氰酸酯基团数量不同等，使得植物油基聚氨酯胶黏剂具有 分子可设计性，更加扩大了此种胶黏剂的使用范围。目前，聚氨酯工业对于植物油多元醇的需求量很大。这些植物油多元醇被广泛的 用于制备各种涂料、胶黏剂、泡沫聚氨酯塑料、快速成型材料和纤维增强复合材料等，但关 于植物油基聚氨酯木材胶黏剂的研究较少且前期研究主要集中于多种植物油多...
【技术保护点】
１．一种可储存的植物油基聚氨酯木材胶黏剂，由以下质量百分比的原料制成：所述的植物油多元醇为本身含有羟基的植物油、经过化学改性后含有羟基的植物油中的一种或两种以上；所述的异氰酸酯为改性的或未改性的具有两个以上异氰酸酯基的化合物；所述的催化剂为有机锡催化剂、胺催化剂中的一种或两种；所述的溶剂为酮、烷基酯、氯代烃或芳香烃。
【技术特征摘要】
【专利技术属性】
技术研发人员：吴，朱锦，刘小青，
申请(专利权)人：中国科学院宁波材料技术与工程研究所，
类型：发明
国别省市：97
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。