The invention discloses a flat back dimension method, which is characterized in that the method comprises the following steps: after the fabric of wool and cotton and the revised vinylon blended, using OpenWidth continuous cooking equipment OpenWidth boil, then the fabric take-up wound around the reel, the reel. Put some time, repeating several times the OpenWidth even boil and reel storage steps in the last OpenWidth even after boiling, not deposited directly on the reel fabric drying by vinylon fabric. Using the method of the invention can make water soluble fiber swelling, swelling, shrinkage, dissolution, ensure the vinylon thoroughly, vinylon fabric cloth smooth, silky hand without loose rotten, indexes of fabric weft tensile strength, tear strength and other properties of warp were able to reach the corresponding national standard requirements.
【技术实现步骤摘要】
本专利技术属于纺织印染工程应用
，尤其涉及一种平幅退维方法。
技术介绍
近年来，高支轻薄化的纺织服装产品已经越来越受到消费者的青睐。在现有环锭 设备上，用高支原料纺制超高支(毛纱120公支及以上，棉纱120英支以上)纱线，用中档原 料纺制高支毛棉纱线，采用水溶性维纶伴纺是有效途径之一。在采用水溶性维纶伴纺加工 高支轻薄织物过程中，织物后整理的退维，即维纶溶解处理是一个很重要的工序。目前退维 工艺主要是选择在煮呢机、匹染机上退维，由于经向张力大，织物不够松弛，退维后织物很 难达到理想的效果。水溶性维纶的溶解过程一般包括吸湿、膨化、收缩、溶解过程，表现在水溶性维纶 伴纺的精纺毛、棉织物上为织物润湿、剧烈收缩伴随手感变硬、之后维纶溶解、织物幅面大 幅胀出、手感松软。目前一般伴纺使用的水溶性维纶纤维在水中的溶解温度是80°C，但由于 水溶性维纶在织物中吸湿困难，膨化和收缩又受到限制，因此成品织物的溶解温度则要在 95 100°C。在这样高温下长时间处理，羊毛、棉纤维不仅其本身受到损伤，而且色彩亦受 到较大影响，特别是条染色织产品。如何使维纶全部溶解，同时不损伤羊毛、棉纤...
【技术保护点】
１．一种平幅退维方法，其特征在于，所述方法包括以下步骤：将经过生修的毛、棉与维纶混纺的坯布，采用平幅连续煮呢设备进行平幅连煮，然后将织物平幅卷绕在卷轴上，将卷轴存放一定时间，重复交替进行多次上述平幅连煮和卷轴存放步骤，在最后一次进行平幅连煮后，不进行卷轴存放而直接对坯布进行烘干得到退维织物。
【技术特征摘要】
1.一种平幅退维方法，其特征在于，所述方法包括以下步骤将经过生修的毛、棉与维 纶混纺的坯布，采用平幅连续煮呢设备进行平幅连煮，然后将织物平幅卷绕在卷轴上，将卷 轴存放一定时间，重复交替进行多次上述平幅连煮和卷轴存放步骤，在最后一次进行平幅 连煮后，不进行卷轴存放而直接对坯布进行烘干得到退维织物。2.根据权利要求1所述的方法，其特征在于，重复平幅连煮次数为3-6次，卷轴存放次 数为2-5次。3.根据权利要求2所述的方法，其特征在于，卷轴存放时间为6-20小时。4.根据权利要求1-3之一所述的方法，其特征在于，所述平幅连煮的步骤包括将毛、 棉与维纶混纺的坯布6-8匹缝接到一起，用引布连续引过3个煮槽，最终将坯布的首尾也缝 接到...
【专利技术属性】
技术研发人员：潘峰，沈兰萍，王俊，