The invention relates to a method of manufacturing the night glow in the functional fabric, the process comprises the following steps: (1) luminous coating paste thickener for preparation: fatty alcohol polyoxyethylene ether, gelatin and oil adding emulsion tank, get thickening agent; then thickening agent and distilled water mixed thickener in the luminescent coating slurry; (2) the luminous coating paste with thickening agent, adhesive, luminous powder and mixed light emitting coating slurry fixing agent, the; (3) the step (2) obtained a luminescent coating slurry and fabric by coating composite in direct coating machine, a luminescent coating coated on the surface of the fabric, coating amount is 60 ~ 70g/m2; the luminous coating fabric coating slurry in 165 ~ 170 degrees under the conditions for 3 to 5 minutes, to obtain the functional fabric light. The functional textiles of the invention can emit bright light at night, and can realize the night luminescence without the aid of auxiliary equipment, thereby reducing the energy consumption.
【技术实现步骤摘要】
本专利技术涉及一种，属于纺织品复合材料制造
技术介绍
夜晚可以发光的功能性织物是工业和民用领域用功能性纺织品之一。此功能性纺织品具有应用价值高，无毒无害，成本低廉，使用寿命长等优点，可广泛应用于航空航海、国防工业、建筑装璜、交通运输、夜间作业、日常生活及娱乐服装等领域。而且，该纺织品在夜晚发出的光无辐射性，是一种环境友好型功能复合材料。目前，国内功能纺织品种类很多， 而且具有优良的价值。但是不借助一定辅助装备在夜晚可以发光的纺织品几乎还没有。在夜晚或黑暗处可以发光的纺织品不仅新颖、美观，而且还具有一定的经济价值。国家每年用于发光所损耗的能源所占比例非常大，而天然能源正在逐渐减少。所以，开发新能源正是形势所迫。
技术实现思路
本专利技术的目的是克服现有技术中存在的不足，提供一种，不借助辅助装备实现夜晚发光，减少能源的损耗。按照本专利技术提供的技术方案，所述，包括以下工艺步骤(1)发光涂层浆用增稠剂的制备将脂肪醇聚氧乙烯醚、明胶和火油按重量比4 4. 5 0. 5 1 7 8. 5加入乳化釜中；在搅拌速度115 120转/分钟、温度60 65°C的条件下处...
【技术保护点】
１．一种在夜晚可以发光的功能性织物的制造方法，其特征是，包括以下工艺步骤：（１）发光涂层浆用增稠剂的制备：将脂肪醇聚氧乙烯醚、明胶和火油按重量比４～４．５∶０．５～１∶７～８．５加入乳化釜中；在搅拌速度１１５～１２０转／分钟、温度６０～６５℃的条件下处理１５～２０分钟，得到增稠剂；再按重量比９５～９６∶４～５将增稠剂和蒸馏水混合，在搅拌速度为６００～７００转／分钟、温度３０～４０℃的条件下搅拌３０～６０分钟，得到所述的发光涂层浆用增稠剂；（２）发光涂层浆的制备：所述发光涂层浆包括以下组份，其组份比例按重量份数计：发光涂层浆用增稠剂 ５～６份，粘合剂：十八烷基异...
【技术特征摘要】