The invention provides a multifunctional coating and method prepared from an oceanic polymetallic nodule crust leaching residue. The paint is composed by grinding and sieving after the ocean polymetallic nodule and crust leaching slag in 19wt% ~ 38wt%, 2wt% ~ 8wt%, zinc yellow mica powder 2wt% to fly ash hollow 8wt% and NiFe2O4 coated beads composite powder 10wt% ~ 20wt% mixture added to epoxy resin solution, ultrasonic milling allowance, get mixed slurry, the mixed slurry of cured epoxy resin curing agent after ultrasonic dispersion was obtained, the amount of curing agent of epoxy resin mixed slurry is 6wt% ~ 9wt%. The efficient use of the silicate solid wastes - ocean polymetallic nodule and crust leaching slag, and the preparation process is simple and easy to implement, reasonable formula design, preparation of coatings with good adhesion, anti rust, anti biological erosion and microwave absorption properties.
【技术实现步骤摘要】
本专利技术涉及一种。
技术介绍
具备良好机械性能与多种功能的新涂料开发一直备受关注。传统技术通过添加人 工合成的铁红来实现防锈功能，以有毒物质的添加来防止生物侵蚀。大洋多金属结核-结 壳浸出渣为锰结核与富钴结壳经氨浸、酸浸提取有价金属后形成的硅酸盐固体废弃物。大 量研究表明大洋多金属结核-结壳浸出渣为纳米结构，并含有大量的铁锰类矿物，具有良 好的防锈、防腐功能。
技术实现思路
本专利技术的目的在于提供一种用大洋多金属结核-结壳浸出渣制备的多功能涂料， 该涂料具有防锈、防生物侵蚀、微波吸收等多种功能。本专利技术的另一个目的在于提供一种以大洋多金属结核-结壳浸出渣为主要功能 填料制备多功能涂料的方法。为了实现上述目的，本专利技术采用以下技术方案一种用大洋多金属结核-结壳浸出渣制备的多功能涂料，该涂料是将经研磨过筛 后的大洋多金属结核-结壳浸出渣、锌黄、云母粉和NWe2O4包覆的粉煤灰空心微珠复合粉 体按照以下配比添加到环氧树脂溶液中混合球磨，形成混合浆料，大洋多金属结核-结壳浸出渣 19wt% 38wt%锌黄2wt% 8wt%云母粉2wt% 8wt%Nii^e2O4包...
【技术保护点】
一种用大洋多金属结核－结壳浸出渣制备的多功能涂料，其特征在于：该涂料是将经研磨过筛后的大洋多金属结核－结壳浸出渣、锌黄、云母粉和ＮｉＦｅ２Ｏ４包覆的粉煤灰空心微珠复合粉体按照以下配比添加到环氧树脂溶液中混合球磨，形成混合浆料， 大洋多金属结核－结壳浸出渣 １９ｗｔ％～３８ｗｔ％ 锌黄 ２ｗｔ％～８ｗｔ％ 云母粉 ２ｗｔ％～８ｗｔ％ ＮｉＦｅ↓［２］Ｏ↓［４］包覆的粉煤灰空心微珠复合粉体 １０ｗｔ％～２０ｗｔ％ 环氧树脂溶液 余量 然后向该混合浆料中添加环氧树脂固化剂固化后超声分散得到的，其中环氧树脂固化剂的添加量为混合浆料的６ｗｔ％～９ｗｔ％。
【技术特征摘要】
【专利技术属性】
技术研发人员：白志民，李桂金，李倩，
申请(专利权)人：中国地质大学北京，
类型：发明
国别省市：11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。