The invention discloses a preparation method of an active semi coke adsorbent. The method comprises the following steps: the raw semi coke pretreatment; the pretreatment for raw semi coke crushing, screening, and selected a certain size of particles; the particle is selected with deionized water flushing times, with a fine powder to remove them, and high temperature drying to constant weight; the in order to particle HNO3 activation, KOH activation and water heating will be activated after chemical activation, particles are washed with deionized water to neutral, and high temperature drying to constant weight, finally obtain the activated semi coke adsorbent. The invention has wide raw material sources, simple preparation process, the adsorbent can well replace activated carbon, experiments show that the adsorption effect of toluene is very good, the adsorption capacity reached 207g toluene /gC, no two pollution in the whole preparation process, in line with the concept of environmental protection.
【技术实现步骤摘要】
本专利技术涉及一种活性半焦吸附剂的制备方法，尤其涉及一种能够替代活性炭用于 净化挥发性工业有机废气的活性半焦吸附剂的制备方法。
技术介绍
目前，利用活性炭为吸附剂来处理工业有机废气中应用最为广泛，但是活性炭存 在着以下的缺点(1)吸附容量低，在使用中需要频繁更换或再生，给操作管理带来不便；成本较高，频繁更换大大增加了运行费用；C3)不能实现根本的再生，必然导致再生不 完全和再生的有机废气处理问题。半焦是由煤低温干馏所得的可燃固体产物，其主要成分是碳、灰分和挥发分。与活 性炭相比，其挥发分含量高，孔隙率大，与一氧化碳、蒸汽等具有较强的反应活性。我国山 西、陕西等省的居民煤气工程多采用直立炉造气，副产大量半焦，这些半焦堆积如山，严重 污染环境。因此，从环境与洁净煤技术利用角度考虑，亟待开发利用这些半焦的新思路和新 产品。本专利技术着眼于改进活性半焦的制备方法和系统，提高其对有机废气的吸附性。
技术实现思路
为了解决上述现有技术中的缺陷，本专利技术提供一种提高吸附容量、实现再生、降低 成本并实现废品再利用的半焦吸附剂的制备方法。为达到上述目的，本专利技术采用了以下技术方案...
【技术保护点】
１．一种活性半焦吸附剂的制备方法，其特征在于，包括：步骤一、对原料半焦进行预处理；所述预处理为将原料半焦粉碎、筛分，并选取其中一定大小的颗粒；步骤二、对选取的所述颗粒用去离子水冲洗多次，用以去除其中的细粉，并高温下烘干至恒重；步骤三、对所述颗粒进行ＨＮＯ３活化，将活化后的颗粒用去离子水洗涤至中性，并高温烘干至恒重；步骤四、对所述颗粒进行ＫＯＨ活化，将活化后的颗粒用去离子水洗涤至中性，并高温烘干至恒重；步骤五、对所述颗粒进行加热水热化学活化，将活化后的颗粒用去离子水洗涤至中性，并高温烘干至恒重；最终获得所述活性半焦吸附剂。
【技术特征摘要】
【专利技术属性】
技术研发人员：李彦旭，杜青平，曾乐民，李丽娟，陈茂濠，李鸿伟，
申请(专利权)人：广东工业大学，
类型：发明
国别省市：81
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。