一种高耐疲劳的玻璃纤维增强尼龙材料及其制备方法技术

本发明专利技术涉及一种高耐疲劳玻璃纤维增强尼龙材料及其制备方法，括以下重量百分比的原料：尼龙树脂48.2％～79.7％、玻璃纤维20％～50％、抗氧剂0.1％～0.6％、润滑剂0.1％～0.6％、成核剂0.1％～0.6％，以上各组分在210～300℃下熔融共混制得高耐疲劳玻璃纤维增强尼龙材料。该方法制备的玻璃纤维增强尼龙材料，具有非常优良的耐疲劳性能，同时具有高度力学性能，良好的表面性能，生产工艺成熟，可以广泛应用于汽车发动机周边和其他行业的零部件的制作。

High fatigue resistant glass fiber reinforced nylon material and preparation method thereof

The invention relates to a high fatigue resistant glass fiber reinforced nylon material and preparation method thereof. The method comprises the following raw materials in percentage by weight: 48.2% to 79.7% nylon resin, glass fiber 20% ~ 50%, 0.1% ~ 0.6%, antioxidant lubricant 0.1% ~ 0.6%, 0.1% ~ 0.6% nucleating agents, each component in the 210 to 300 DEG C melting prepared high fatigue resistant glass fiber reinforced nylon material. The method of preparation of glass fiber reinforced nylon material, has very excellent anti fatigue performance, and high mechanical properties, good surface properties, mature production technology, production can be widely used in automotive and other industries around the engine parts.

【技术实现步骤摘要】

本专利技术涉及，可应用于汽车 工业和各种需要高耐疲劳玻璃纤维增强尼龙的行业，属于高分子材料
具体而言， 该尼龙材料优先应用于需要高耐疲劳的部件，尤其像汽车发动机周边零件，如进气歧管、发 动机罩盖、气门室罩盖和空滤器等等。
技术介绍
尼龙树脂具有较高的机械强度、耐热性、自润滑性、优良的阻隔性能和耐化学腐蚀 等优异的综合性能，广泛的应用于机械制造业，电子电器和交通运输等领域，其用量目前居 于五大工程塑料之首。尼龙材料一般包括PA6，PA66，PAlO 10，PAll，PA12，PA46，PA6T，PA9T 和PAlOT等。在汽车和其他行业中使用最多的材料是PA6和PA66。由于很多的功能部件， 在正常运作时候，需要不停得震动，非常考虑材料的耐疲劳性能。现有的很多尼龙改性材 料，并没有实际去考虑耐疲劳的问题。近年来，市场对材料的性能要求越来越高，耐疲劳的 要求逐渐提上日程。已有公开的专利CN 1854287提到工程塑料(PA)改性研究，但是针对耐疲劳性并 没有展开说明材料的耐疲劳性能达到什么程度。专利CN 1508358A和CN 101412845A都提 到玻纤增强的尼龙材料，但本文档来自技高网...

【技术保护点】
一种高耐疲劳的玻璃纤维增强尼龙材料，其特征在于，包括以下重量百分比的原料：　　尼龙树脂　４８．２％～７９．７％　　玻璃纤维　２０％～５０％　　抗氧剂　０．１％～０．６％　　润滑剂　０．１％～０．６％　　成核剂　０．１％～０．６％。

【技术特征摘要】

【专利技术属性】
技术研发人员：冯德才，丁正亚，孙雅杰，梁惠强，
申请(专利权)人：上海金发科技发展有限公司，金发科技股份有限公司，
类型：发明
国别省市：31