The invention discloses a high Mn MnAlSiTi alloy titanium content, the mass percent content of each chemical component of the MnAlSiTi alloy is Mn40% ~ 55%, Al12~18%, Si13% ~ 22%, Ti1% ~ 12%, the rest is Fe and impurity elements. The process of preparation of the alloy is waste aluminum, titanium iron, aluminum, silicon manganese alloy and slag according to the elemental requirements in accordance with the sequence of weighing, ash, waste aluminum, titanium iron, silicon manganese alloy, pure aluminum are added smelting induction furnace; solidification with slow fast slow way. The invention relates to a method for preparing high manganese alloy, titanium content is high, can relax the raw material of carbon and other impurities into the furnace content range, low cost; the preparation of alloy can be stored in a variety of climatic conditions, the structural stability of powder. The alloy has the advantages of strong deoxidization ability, high impurity removal rate, good alloying effect and good fatigue and seismic resistance of the steel.
【技术实现步骤摘要】
本专利技术涉及炼钢用中间合金
，具体涉及一种锰基高钛含量的MnAlSiTi 合金及其制备方法，该合金可用于抗震钢、不锈钢、含钛钢等的钢液脱氧与合金化。
技术介绍
锰系中间合金作为炼钢中必不可少的原料，与钢铁行业的发展息息相关。在我国 钢铁行业高速发展的大环境下，锰系中间合金的需求量急剧增加。但在2008年全球金融危 机影响下，我国钢铁行业面临产能过剩、节能减排和产业结构调整等重大发展课题，钢铁企 业开始注重低碳、绿色、环保和高值生产。近年来科技工作者为了实现国家战略需求，在开发高附加值新品种钢、如不锈钢、 重轨钢、抗震钢等方面做了大量卓有成效的工作，在改进冶炼工艺的同时，专利技术了利用系列 锰系中间合金进行钢液的复合脱氧、去气、排除夹杂、合金化的方法，从而优化钢材性能。但 铝锰钛中间合金制备过程中表现出合金元素烧损率高，制备完成后储存中容易时效粉化， 这一系列问题大大制约了此类合金的工业实用性。现有技术中，公开的专利技术专利大多注重于铝锰中间合金的元素多元化，比如中国 专利CN1160087公开的合金Mn彡35%，Al彡18%，却未提及合金粉化问题。事实上...
【技术保护点】
一种锰基高钛含量的ＭｎＡｌＳｉＴｉ合金，其特征在于，所述ＭｎＡｌＳｉＴｉ合金中各化学成分的质量百分含量为：Ｍｎ ４０％～５５％，Ａｌ １２～１８％，Ｓｉ １３％～２２％，Ｔｉ １％～１２％，余量为Ｆｅ以及杂质元素。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。