The invention relates to a method for rolling Cr17 ferritic stainless steel wire, which orderly comprises the following steps: I will Cr17 ferritic stainless steel is heated to 1080-1130 DEG II; the heating of Cr17 ferritic stainless steel billet, wire to rolling made of wire, full line temperature control when rolling is 850-900 DEG C; III will be sent to the wire feeding machine, wire feeding machine in the spinning temperature is 850-900 DEG C; IV after silking, rapid cooling to 700-800 deg.c, insulation table insulation for 2-4 minutes by V; then, quickly cooled to 300 DEG C or below 300 DEG C. This method has the advantages of rolling annealing process Cr17 ferritic stainless steel wire, reduce the tensile strength of rolled wire to 480Mpa.
【技术实现步骤摘要】
本专利技术涉及一种含铬铁素体不锈钢线材的轧制方法，具体讲是一种Crl7型铁素 体不锈钢线材的轧制方法。
技术介绍
在国内，只有少数企业生产不锈钢线材，特别是生产铁素体不锈钢线材的企业更 少。现有的Crl7型铁素体不锈钢线材的轧制方法在轧制后强度偏高，存在轧制应力，直接 使用会影响加工效率、增加模具消耗，可能存在晶间腐蚀问题；通过退火处理可消除上述缺 陷，但退火处理会增加费用，有可能造成晶粒粗大，影响后续使用。
技术实现思路
为了克服现有Crl7型铁素体不锈钢线材的轧制方法的上述不足，本专利技术提供一 种能消除轧制应力的Crl7型铁素体不锈钢线材的轧制方法。本Crl7型铁素体不锈钢线材的轧制方法包括下述依次的步骤I将Crl7型铁素体不锈钢加热到1080-1130°C ；II把加热的Crl7型铁素体不锈钢坯，送到线材连轧机轧制成线材，轧制时的全线 温度控制为850-900°C ；III将线材送到吐丝机，线材在吐丝机的吐丝温度为850°C -900°C ；IV吐丝后，快速冷却到700°C -800°C，利用保温辊道保温2_4分钟；V然后，立即快速冷却到300°C或300°...
【技术保护点】
１．一种Ｃｒ１７型铁素体不锈钢线材的轧制方法，它包括下述依次的步骤：Ｉ将Ｃｒ１７型铁素体不锈钢加热到１０８０－１１３０℃；ＩＩ把加热的Ｃｒ１７型铁素体不锈钢坯，送到线材连轧机轧制成线材，轧制时的全线温度控制为８５０－９００℃；ＩＩＩ将线材送到吐丝机，线材在吐丝机的吐丝温度为８５０℃－９００℃；ＩＶ吐丝后，快速冷却到７００℃－８００℃，利用保温辊道保温２－４分钟；Ｖ然后，立即快速冷却到３００℃或３００℃以下。
【技术特征摘要】
【专利技术属性】
技术研发人员：叶文学，李颖，姚文峰，杨丽俊，
申请(专利权)人：山西太钢不锈钢股份有限公司，
类型：发明
国别省市：14