本发明专利技术涉及一种吸附材料，解决了液体电热驱蚊器用芯棒的堵塞、不能用加工方法设定挥发速率的问题。其主要技术特征是采用聚乙烯醇缩甲醛泡沫塑料或软质聚氨酯泡沫塑料或聚乙烯醇缩甲醛泡沫塑料和软质聚氨酯泡沫塑料作为液体电热驱蚊器用芯棒材料及将上述两种泡沫塑料中的一种或两种与非吸附性材料共同构成芯棒。本发明专利技术用于液体电热驱蚊器用芯棒。（*该技术在2022年保护过期，可自由使用*）

Mandrel for liquid electric heating mosquito repellent

The invention relates to an adsorption material, which solves the problem that the core rod of a liquid electric mosquito repellent device is blocked and the volatilization rate can not be set by the processing method. The technology is mainly characterized by polyvinyl formal foam or soft polyurethane foam or polyvinyl formal foam and soft polyurethane foam as a liquid electric mosquito heater with mandrel material and the above two kinds of foam in one or two and non absorbent material composed of mandrel. The present invention relates to a mandrel for liquid electric heater. \ue5cf

【技术实现步骤摘要】
本专利技术涉及一种吸附材料。液体电热驱蚊器用芯棒(以下简称芯棒)一般用多孔状石墨、陶瓷等制成。(参见《新编家用电热器具大全》王文超等编、459P、三、液体电热驱蚊器节)。近年，国外出现塑料芯棒如超高分子量聚乙烯烧结芯棒。(有关技术见日本公開特许1996、216264番号“超高分子量ポリエチレン製多孔质体の製造方法”及特開平7-52263“プヲスチック製多孔质筒状体の成形方法”。分类B29K105/04)。芯棒形状一般为直径7～7.15mm，高72～73mm的圆柱体。作用是吸附驱蚊剂并加以挥发。原理是一端朝下插入药液瓶内的驱蚊剂中，另一端朝上插在电热环中，驱蚊剂因芯棒微孔的虹吸作用由下爬升至朝上一端，受电热环加热汽化，挥发驱蚊。特点是朝上一端与80℃以上有机溶剂接触。基本使用要求一、一种芯棒的挥发速率(单位时间挥发量)一定；二、挥发速率符合使用要求。但现有芯棒无法给予满足，原因是存在二大难题一、堵塞。石墨、陶瓷类芯棒因微孔闭孔率高，驱蚊剂内溶质一旦在朝上一端遇闭孔堵塞而阻滞后，会过热碳化，加剧堵塞，引发更多溶质碳化，形成恶性循环，挥发速率随之下降直至为零。而塑料芯棒则因朝上一端与80℃以本文档来自技高网...

【技术保护点】
一种液体电热驱蚊器用芯棒，其特征在于：采用聚乙烯醇缩甲醛泡沫塑料或软质聚氨酯泡沫塑料或聚乙烯醇缩甲醛泡沫塑料和软质聚氨酯泡沫塑料作为液体电热驱蚊器用芯棒的材料。

【技术特征摘要】
1.一种液体电热驱蚊器用芯棒，其特征在于采用聚乙烯醇缩甲醛泡沫塑料或软质聚氨酯泡沫塑料或聚乙烯醇缩甲醛泡沫塑料和软质聚氨酯泡沫塑料作为液体电热驱蚊器用芯棒的材料。2.根据权利要求1所述的液体电热驱蚊器用芯棒，其特征在于将...