The present invention provides an aqueous soft rubber and a preparation method thereof and application of plastic plastic composite adhesive, the waterborne soft gum is mainly composed of acrylic acid, butyl acrylate, styrene, functional monomer, initiator, emulsifier, buffering agent, functional additives, pH adjusting agent, softening water through the reaction of these materials prepared. The invention adopts water medium, no pollution, eliminate the production and use of personnel from harmful organic solvents on the body, and the fire in the process of using the risk is greatly reduced, and no residue of harmful substances in the composite membrane; improve the cohesion of the film, solve the balance between cohesion and adhesion and the bond strength, bond strength, can overcome the product flow equality operation problem composite, and the composite good products without curing can be cut, shorten the production time of composite.
【技术实现步骤摘要】
本专利技术涉及一种应用与塑塑复合材料胶粘的软包胶，尤其涉及一种
技术介绍
软包胶是指在一般厚度在30iMTl内的塑塑复合，应用范围非常广泛，常见于食品、医药、日用品的包装。软包复合所用的胶粘剂分为油性、醇溶性和水性三种，其中油性胶的毒性和使用安全性问题越来越突出，这是由于油性胶中使用的溶剂为甲苯、二甲苯，固化剂中使用异氰酸酯类物质，不但环境污染大，对操作工人的健康伤害大，而且在烘干过程中的大量挥发，极易造成火灾，同时，在复合好的成品中容易有残留，易渗透至内层物品，造成二次污染，因此，软包复合中油性胶必然会被淘汰。醇溶性软包胶虽然在溶剂中没有苯类物质，但大量的醇类物质仍然会造成污染和危险，而且成本也较高，属于过渡产品，用水性软包胶进行复合已是大势所趋。水性软包胶虽然安全、环保，但其合成技术难度大，国内在此几乎是空白，虽然有个别厂家推出水性软包胶水，其性能仍无法达到油性胶的效果，而且只能适合部分薄膜的复合，无法满足塑塑软包复合多种薄膜的要求。
技术实现思路
本专利技术的目的，就是为了解决上述问题而提供一种水性软包胶。本专利技术的另一个目的在于提供一种制备本专利技术水性软...
【技术保护点】
一种水性软包胶，由以下组分通过反应制备而成：丙烯酸，丙烯酸丁酯，苯乙烯，功能性单体，引发剂，乳化剂，缓冲剂，功能性助剂，ｐＨ调整剂，软化水； 所述的功能性单体选自邻苯二甲酸二烯丙酯、丙烯酸羟乙酯和Ｎ－羟甲基丙烯酰胺中的至少一种； 所述的引发剂为过硫酸盐； 所述的乳化剂选自磺基琥珀酸盐和酚醚硫酸盐中的至少一种； 所述的缓冲剂选自碳酸氢铵和碳酸氢钠中的至少一种； 所述的功能性助剂选自ＯＴ７５、矿物油和水溶性丙烯酸树脂中的至少一种； 所述的ｐＨ调 整剂为氨水； 上述各组分所占的重量百分比分别为：丙烯酸１～１０％，...
【技术特征摘要】
【专利技术属性】
技术研发人员：刘国富，赵永旗，毛继明，戚向东，
申请(专利权)人：上海奇想青晨化工科技股份有限公司，
类型：发明
国别省市：31[中国|上海]