MeAPSO-44分子筛及其合成方法技术

一种ＭｅＡＰＳＯ－４４分子筛，其无水基化学组成可表示为：ｍＲ.ｎＭｅ（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］，其中Ｒ为存在于分子筛微孔中的模板剂，ｍ为每摩尔（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］中Ｒ的摩尔数，且ｍ＝０．０３～３．００；ｘ、ｙ、ｚ分别为Ｓｉ、Ａｌ、Ｐ原子的摩尔分数，且满足ｘ＋ｙ＋ｚ＝１，同时，ｘ＝０．２～０．６０，ｙ＝０．０１～０．６０，ｚ＝０．０１～０．６０；Ｍｅ为进入分子筛中的金属原子，ｎ为每摩尔（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］中Ｍｅ的摩尔数，ｎ＝０．０１～０．６０。该分子筛可以通过加入金属化合物的量调变表面酸性，从而能够大大提高其在催化反应过程中的性能。（*该技术在2019年保护过期，可自由使用*）

MeAPSO-44 molecular sieve and synthesis method thereof

A MeAPSO 44 molecular sieve, the water-based chemical composition can be expressed as: mR.nMe (Si: X Al: y P: Z: O) 2, where R is present in molecular sieve template micropore, m per mole (Si: X Al: y P: Z O), the number of moles of 2: R, and M = 0.03 ~ 3; X, y and Z were Si, Al, the mole fraction of P atoms, and satisfy the X + y + Z = 1, at the same time, x = 0.2 ~ 0.60. Y = 0.01 ~ 0.60, z = 0.01 ~ 0.60; Me for metal atoms into the molecular sieve, N per mole (Si: X Al: y P: z): O 2 Me mole number, N = 0.01 to 0.60. The zeolite can modify the surface acidity by adding the amount of the metal compound, thereby greatly improving the performance in the catalytic reaction process.

【技术实现步骤摘要】

本专利技术提供了一种MeAPSO-44分子筛及其合成方法。美国专利USP 4,440,871曾公开了几种磷酸硅铝分子筛的合成方法，其技术特点是采用硅源、铝源、磷源以及不同的模板剂合成出了一类SAPO分子筛，其中一些小孔结构的分子筛如SAPO-34等已成功应用于MTO(甲醇制取低碳烯烃)或SDTO(合成气经由二甲醚制取低碳烯烃)等过程，但SAPO-44分子筛的应用报导较少。SAPO-44分子筛由磷、硅、铝和氧组成了类菱沸石结构，其结构单元由PO2+、AlO2-和SiO2四面体组成。无水化学组成式可表示为mR:(SixAlyPz)O2，其中R为存在于分子筛微孔中的模板剂，m为每摩尔(SixAlyPz)O2中R的摩尔数，x、y、z分别为Si、Al、P的摩尔分数，且满足x+y+z=1。本专利技术的目的在于提供一种MeAPSO-44分子筛及其合成方法，这类分子筛可以通过加入的金属化合物的量调变其表面酸性，从而能够大大改善其催化反应性能。本专利技术提供的MeAPSO-44分子筛，其特征在于所合成分子筛的无水基化学组成可表示为mR·nMe:(SixAlyPz)O2，其中R为存在于分子筛微孔中本文档来自技高网...

【技术保护点】
一种ＭｅＡＰＳＯ－４４分子筛，其特征在于无水基化学组成可表示为：ｍＲ.ｎＭｅ（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］，其中Ｒ为存在于分子筛微孔中的一种模板剂，ｍ为每摩尔（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］中Ｒ的摩尔数，且ｍ＝０．０３～３．００；ｘ、ｙ、ｚ分别为Ｓｉ、Ａｌ、Ｐ原子的摩尔分数，且满足ｘ＋ｙ＋ｚ＝１，同时，ｘ＝０．２～０．６０，ｙ＝０．０１～０．６０，ｚ＝０．０１～０．６０；Ｍｅ为存在于分子筛中的金属杂原子，ｎ为每摩尔（ＳｉｘＡｌｙＰｚ）Ｏ↓［２］中Ｍｅ的摩尔数，ｎ＝０．０１～０．６０。

【技术特征摘要】

【专利技术属性】
技术研发人员：李宏愿，刘中民，孙承林，许磊，杨立新，黄韬，
申请(专利权)人：中国科学院大连化学物理研究所，
类型：发明
国别省市：91[中国|大连]