The invention provides a preparation method of indium tin oxide nano powder including: ratio of indium and tin is 9: 1~10: four indium chloride chloride 1 hydrate and five water tin is dissolved in deionized water, adding solution, mixing the reaction solution; the reaction solution into the reaction kettle in 3, 150~200 DEG C ~ 18h, natural cooling to room temperature to obtain an intermediate product; the intermediate product of centrifugal separation, deionized water, ethanol washing, drying product at 40~70 DEG C for 6 ~ 24h ITO precursor; ITO precursor calcined, from room temperature to 400~550 DEG C, the heating rate is 2~8 C / min, 1~3 hours, natural cooling to room temperature, ITO nano powder. The prepared ITO nanometer powder has the advantages of high purity, small particle size, even component, simple synthesis process and required production equipment and easy realization of industrial production.
【技术实现步骤摘要】
本专利技术属纳米粉体
，特别是涉及。
技术介绍
伴随着液晶显示的发展，用于透明电极的铟锡氧化物需要量急剧增加。目前，世界上的发达国家都将一半左右的铟用于制备IT0材料。纳米ITO作为一种n型简并半导体，对可见光透明，能强烈反射红外光，良好的导电性能，与基体较好的结合能力和良好的化学稳定性越来越受到关注，因而在平面显示器(LCD, OLED)、太阳能电池、传感器、功能性玻璃等方面获得日益广泛的应用。 ITO纳米粉体的制备方法很多，可分为物理法、化学法和物理化学法。按物质的原始状态可分为固相法、液相法和气相法。如机械混合法、喷雾热解法、化学沉淀法、溶胶凝胶法、水热法和微乳法等。Richard A.等在Advanced Materials, 4163， 20， (2008)上报道了用In(Ac)3和Sn(Ac)2做原料，在氩气保护下在胺溶液中合成了非团聚的纳米铟锡氧化物，结果表明此法制备的ITO具有很好的分散性。Shuguang Chen等在Materials Letters,1342,59， (2005)上报道了用一种改进的化学沉淀法制备了 ITO纳米针状物，...
【技术保护点】
一种铟锡氧化物纳米粉体的制备方法，包括： （１）反应溶液的配制 在室温下，称取铟和锡的摩尔比为９∶１～１０∶１的四水氯化铟和五水氯化锡用去离子水溶解，然后加入乙二胺溶液，混合均匀得到反应溶液； （２）溶剂热反应 将步骤（１）中的反应溶液放入反应釜中，在１５０～２００℃反应３～１８ｈ，自然冷却至室温得到中间产物； （３）产品分离、洗涤、干燥 将中间产物离心分离，转速为６０００～８０００ｒｐｍ，时间为３～２０ｍｉｎ，用去离子水洗涤至无Ｃｌ－为止，无水乙醇洗涤１～３次，产物在４０～７０℃烘干６～２４ｈ得到ＩＴＯ前躯体； （４）煅烧 将得到的ＩＴＯ前驱体进行煅烧，从...
【技术特征摘要】
【专利技术属性】
技术研发人员：李耀刚，朱冰洁，王宏志，张青红，朱美芳，
申请(专利权)人：东华大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。