MeAPSO-18分子筛及其合成方法技术

一种分子筛ＭｅＡＰＳＯ－１８无水化学组成可表示为：ｍＲ.ｎＭｅ.（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］，其中Ｒ为存在于分子筛微孔中的模板剂，ｍ为每摩尔（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］中Ｒ的摩尔数，且ｍ＝０．００１～０．３；ｘ、ｙ、ｚ分别为Ｓｉ、Ａｌ、Ｐ的摩尔分数，其范围是ｘ＝０．００１～０．９８，ｙ＝０．０１～０．６０，ｚ＝０．０１～０．６０；且满足ｘ＋ｙ＋ｚ＝１，Ｍｅ为金属原子，ｎ为每摩尔（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐｚ）Ｏ↓［２］中Ｍｅ的摩尔数；ｎ＝０．０１～０．２５。该分子筛具有离子交换性能和吸附性能，对于甲醇转化制低碳烯烃等反应均具有较高的催化活性。（*该技术在2019年保护过期，可自由使用*）

MeAPSO-18 molecular sieve and synthesis method thereof

A molecular sieve MeAPSO 18 anhydrous chemical composition can be expressed as: mR.nMe. (Si: X Al: y P: Z: O) 2, where R is present in molecular sieve template micropore, m per mole (Si: X: Al. Y: P: Z: O), the number of moles of R 2, and M = 0.001 ~ 0.3; X, y and Z were Si, Al, the mole fraction of P, which is in the range of x = 0.001 ~ 0.98, 0.01 ~ y = 0.60, z = 0.01 ~ 0.60; and meet Xyz = 1, Me n for each metal atom, Moore (Si: X Al: y Pz O), the number of moles of 2: Me; n = 0.01 ~ 0.25. The zeolite has the characteristics of ion exchange and adsorption, and has high catalytic activity for the conversion of methanol to low carbon olefins.

【技术实现步骤摘要】

本专利技术涉及一种新型小孔磷酸硅铝分子筛MeAPSO-18及其合成方法。1984年，美国专利USP 4,440,871公开了几种磷酸硅铝分子筛的合成方法，其技术特点是采用硅源、铝源、磷源以及不同的模板剂合成出了一系列SAPO分子筛，其中一些小孔结构的分子筛如SAPO"C4等已成功应用于甲醇转化制低碳烯烃(MTO)等过程，显示出很好的催化性能。这类分子筛由磷、硅、铝和氧组成了类菱沸石结构，其结构单元由PO2、AlO2和SiO2四面体组成。其无水化学组成式可表示为mR·(SixAlyPz)O2，其中R为存在于分子筛微孔中的模板剂，m为每摩尔(SixAlyPz)O2中R的摩尔数，x、y、z分别为Si、Al、P的摩尔分数，且满足x+y+z=1。但是上述专利没有涉及SAPO-18分子筛的合成。在这以后，随着人们对SAPO系列分子筛的不断关注，一些不同的SAPO系列分子筛相继被合成出来。但是有关杂原子MeAPO-18分子筛的报导较少。本专利技术的目的在于提供一种新型小孔杂原子磷酸硅铝分子筛MeAPSO-18及其合成方法。通过在SAPO-18分子筛骨架中引入金属杂原子，使其催化性质和吸附性质本文档来自技高网...

【技术保护点】
一种磷酸硅铝分子筛ＭｅＡＰＳＯ－１８，其特征在于无水化学组成可表示为：ｍＲ.ｎＭｅ.（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］，其中Ｒ为存在于分子筛微孔中的一种模板剂，ｍ为每摩尔（Ｓｉ↓［ｘ］Ａｌ↓［ｙ］Ｐ↓［ｚ］）Ｏ↓［２］中Ｒ的摩尔数，且ｍ＝０．００１～０．３；ｘ、ｙ、ｚ分别为Ｓｉ、Ａｌ、Ｐ的摩尔分数，其范围是ｘ＝０．００１～０．９８，ｙ＝０．０１～０．６０，ｚ＝０．０１～０．６０，且满足ｘ＋ｙ＋ｚ＝１，Ｍｅ为金属原子，ｎ为每摩尔（ＳｉｘＡｌｙＰｚ）Ｏ↓［２］中Ｍｅ的摩尔数，ｎ＝０．０１～０．２５。

【技术特征摘要】

【专利技术属性】
技术研发人员：黄韬，刘中民，许磊，孙承林，田鹏，李宏愿，
申请(专利权)人：中国科学院大连化学物理研究所，
类型：发明
国别省市：91[中国|大连]