The invention relates to a preparation method of potassium dihydrogen phosphate (KDP) twins, it is if a temperature lowering method of twin artificial culture method by aqueous solution of inorganic crystal material preparation technology field. The main process method of the invention is as follows: the potassium dihydrogen phosphate (KDP) crystal shape complete cut two cone top, cut the remaining part of the two paragraph, according to the established flat angle direction, into the same size of two crystals, the docking corresponding to the surface grinding of the same size, and then to the next two top and then polished; for twin interface formation at the contact surface along the diagonal grinding, and polishing; then two crystal two conical contact, the two cone at a straight line; YZ flat bottom vertical paste into the organic glass plate; then put glue crystals into KDP saturated solution, control the growth condition. The crystal growth in the last two, generating 40 degrees KDP coaxial twin.
【技术实现步骤摘要】
本专利技术涉及一种磷酸二氢钾(KDP)孪晶的制备方法，它主是要是一种采用水溶液 降温法人工培养孪晶的方法，属无机晶体材料制备工
技术介绍
近些年来，有关"负折射率"人工媒质的研究成为一个引人注目的前沿领域，并引 发了许多的可能应用。在一定入射角范围内，孪晶界面对光波有等效负折射和全透射现象。 由此，我们可以自主设计孪晶结构，使孪晶界面实现全角度内的等效负折射现象，并尽可能 地补偿晶体的色散和双折射，以实现超透镜的应用。同时，我们还可以优化孪晶结构，实现 滤波、波分复用、角色散、色散补偿、电光调制器件等用途，其应用前景非常的有潜力。自然 界天然孪晶比较少，质量也不高；采用"光胶"方法，将两块定向切割的单晶制成的孪晶不完 美，对光波有一定散射。目前，没有找到有关KDP孪晶培养方法的报道。因此，我们借鉴KDP 单晶生长技术，以磷酸二氢钾为原料，对人工培养定向孪晶进行探索。按照孪晶结构设计的 要求，我们采用水溶液降温法培养两光轴成相应角度的定向KDP孪晶。
技术实现思路
本专利技术的目的是针对目前自然然孪晶稀少，质量不高，而用"光胶"技术制成的孪 晶，其界面不完...
【技术保护点】
一种磷酸二氢钾孪晶的制备方法，主要采用水溶液降温法，该方法具有以下的制备过程和步骤：ａ．将外形完整的磷酸二氢钾（ＫＤＰ）晶体切掉两锥顶，剩下的部分切取两段，用细砂纸将这两段晶体按既定角度方向磨好，再用细砂纸磨去晶体表面的微晶，两段晶体磨成大小相同，接着用细软的丝绸抛光晶体。将磨出的大小相同的对应面重合，把上下两顶磨平，再沿ｘｙ平面内矩形的对角线将籽晶磨掉一半，即把与欲形成的孪晶界面沿上述对角线相正交的面磨大；ｂ．磨好后将晶体抛光，然后将处理好的两段晶体，使其两锥面接触，两锥面处在一条支线上，并以ｙｚ平面为底竖直粘贴到有机玻璃板上；ｃ．配制好磷酸二氢钾（ＫＤＰ）饱和溶液：溶质...
【技术特征摘要】
【专利技术属性】
技术研发人员：王燕，徐军，刘燕红，庞宛文，白丽华，张惠芳，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[中国|上海]