The invention discloses a middle temperature latent curing agent for epoxy resin and a preparation method thereof, wherein the compound is characterized in that the structure is composed of cyclopentadienyl iron N alkyl carbazole and ferric salt. The compounds with two ferrocene and N-alkyl substituted carbazole as raw material, through the Lewis acid catalyzed ligand exchange reaction occurred prepared. As latent curing agents, these compounds can initiate epoxide polymerization at moderate temperatures and have excellent thermal initiation and latent heat properties. The introduction of alkyl causes the solubility of these compounds in non-polar resins to be enhanced significantly, and has broad research potential and application prospect in the field of epoxy resin application.
【技术实现步骤摘要】
本专利技术涉及一类中温潜伏性热固化剂的制备和应用，特别涉及一类用于环 氧化合物的热固化引发剂的制备和应用。
技术介绍
环氧树脂是一类具有良好黏结、耐腐蚀、绝缘、高强度等性能的热固性高分 子合成材料，广泛应用于多种金属和非金属材料的黏结、耐腐蚀涂料、电器绝缘 材料、玻璃钢/复合材料的制造等方面，在电子、电气、机械制造、化工防腐及 其他许多工业领域中起着重要的作用，已成为各工业领域中不可缺少的基础材 料。常用的环氧固化体系是双组分体系，固化剂常用酸酐和胺类物质，双组分体 系存在以下缺点配置过程烦琐；配料混合不均匀，固化性能会发生波动；计量 上的误差难以避免等等。潜伏性固化剂是指室温下在环氧树脂中能长时间稳定存在，而在加热等作用 下能迅速引发固化反应的化合物体系。环氧树脂潜伏性固化剂是配制单组分环氧 树脂体系的原料。已开发的环氧树脂潜伏性固化剂的种类很多，主要有三氟化硼 络合物、三聚氰胺及其衍生物、咪唑衍生物和有机酰肼类等，但是每种类型的固 化剂都有一定的优点和缺点，到目前为止，仍然没有发现一种性能特别优良，十分 理想的潜伏性固化剂。优良的环氧树脂潜伏性固化剂要求具...
【技术保护点】
一类环氧树脂中温潜伏性热固化剂，该类化合物具有环戊二烯－铁－Ｎ－烷基咔唑茂铁盐结构，其化学结构通式如下式： ＊＊＊ Ｒ、Ｒ’、Ｒ”和Ｒ”’为Ｈ、烷基、烯基、苯环、取代苯环、萘环或取代萘环，Ｒ’、Ｒ”和Ｒ”’取代基的数目ｎ是１－６ ，Ｘ↑［－］为非亲核性阴离子如：ＳｂＦ↓［４］↑［－］，ＡｓＦ↓［６］↑［－］，ＰＦ↓［６］↑［－］，ＢＦ↓［４］↑［－］，ＣＦ↓［３］ＳＯ↓［３］↑［－］或ＣＨ↓［３］ＳＯ↓［３］↑［－］。
【技术特征摘要】
【专利技术属性】
技术研发人员：王涛，李治全，李蒙，卢明宝，
申请(专利权)人：北京化工大学，
类型：发明
国别省市：11[中国|北京]