用于尿道修复的聚乙交酯（ＰＧＡ）编织型泌尿管支架的制备方法技术

本发明专利技术涉及一种用于尿道修复的聚乙交酯（ＰＧＡ）编织型泌尿管支架支架，该支架采用二维三轴向的编织方法制备，具体包括：（１）取４８ｔｅｘ的聚乙交酯（ＰＧＡ）长丝，将ＰＧＡ编织于芯棒上，其齿轮比为１３２／２８，机速设为６至７；（２）在９０～１０５℃定型５ｍｉｎ；（３）将ＰＧＡ编织层从芯棒上退下，在２．５ｗｔ％－３ｗｔ％壳聚糖浆液中浸渍３０分钟，自然晾干后，在－５０℃的冷冻干燥环境下４小时，即得。本发明专利技术制备方法简单，成本低；所得编织型泌尿管支架具有仿生泌尿管的表观形态，支架降解完全。

Preparation method of poly (lactide) (PGA) braided type urinary catheter bracket for urethral repair

The invention relates to a method for repairing urethral polyglycollide (PGA) braiding urethral scaffold support system, weaving method of the bracket by three dimensional axial preparation, including: (1) 48tex polyglycollide (PGA) filament, PGA woven on a mandrel, the gear ratio is 132 / 28, the machine speed is set to 6 to 7; (2) at 90 to 105 DEG C type 5min; (3) PGA woven layer on the mandrel from the back, in the 2.5wt% 3wt% chitosan slurry soaking for 30 minutes, naturally dried, frozen in dry environment under 50 DEG C for 4 hours, that is. The preparation method of the invention is simple and the cost is low; the knitted type urinary catheter bracket has the apparent appearance of the bionic urinary catheter, and the stent is degraded completely.

【技术实现步骤摘要】

【技术保护点】
一种用于尿道修复的聚乙交酯编织型泌尿管支架，该支架采用二维三轴向的编织方法制备，具体包括：　　　　（１）取４８ｔｅｘ的聚乙交酯ＰＧＡ长丝，为７股复丝，每股１２根单纤，用１６锭锭子编织机将ＰＧＡ编织于芯棒上，其齿轮比为１３２／２８，机速设为６至７；　　　　（２）上述在９０～１０５℃定型５ｍｉｎ；　　　　（３）将上述ＰＧＡ编织层从芯棒上退下，在２．５ｗｔ％－３ｗｔ％壳聚糖浆液中浸渍３０分钟，自然晾干后，在－５０℃的冷冻干燥环境下４小时，裁为２ｃｍ段。

【技术特征摘要】

【专利技术属性】
技术研发人员：陈南梁，沈志静，张佩华，王文祖，郯志清，
申请(专利权)人：东华大学，
类型：发明
国别省市：31[中国|上海]