The invention belongs to the technical field of flexible electrode materials, and relates to a preparation method of flexible medical silver electrode materials. The first step of the modified polymer surface, into the surface active groups, and then under the effect of ultrasonic electroless silver plating; active group and silver plating by chemical bonds, the adhesion density of silver coating and polymer materials are greatly enhanced, the peel strength of coating is greater than 40N / cm; after the SBF test flexible, electrode material prepared has strong corrosion resistance. The electrode material has high safety factor, and can be widely used for interventional treatment in clinical medicine, such as repeated treatment of esophagus cancer and congenital heart disease.
【技术实现步骤摘要】
本专利技术属于医用材料
，具体涉及。
技术介绍
介入疗法是介于内科和外科之间的一种新的治疗方法，它是在电视屏幕图像的引 导下，利用一些特殊材料制成的导管、球囊、支架等器材，经动脉血管、静脉血管、食管等人 体腔道或在人体上扎针建立通道，进入病变部位，利用电生理剌激、动/静脉扩张等手段对 疾病进行诊断与治疗。该疗法不用开刀，只对病变进行治疗，创伤小，见效快，时间短，副作 用小，对某些疾病可以进行重复治疗。介入疗法对治疗先天性心脏病效果显著。介入治疗 学在国外始于上世纪60年代末，我国80年代初期开始应用，但发展迅速，某些方面已达到 或接近国外先进水平。(S.Chen，et al. P. Natl. Acad. Sci. USA 106 (23) (2009) 9180-9184. A. Petri, et al. Cancer Res. 69 (2) (2009)393—395.) 但介入疗法存在电极材料不理想的问题。目前采用的介入疗法电极为金属柱状电 极，该种电极表面积小且硬度高，介入治疗时患者痛苦较大，治疗时间较长，因此急需研制 出一种柔性的电极材料以减缓...
【技术保护点】
一种柔性医用银电极材料的制备方法，其特征在于具体步骤为： （１）清洁基板：将聚合物基板洗净、烘干； （２）基板表面活化：将清洁后的基板浸泡在活化溶液中３０～６０分钟，取出洗净，烘干； （３）超声波作用下化学镀银：最后将活化后的基板浸泡在银化学镀液中，于１２０Ｗ，４０ＫＨｚ的超声波作用下，在２０～２５℃化学镀２０～３０分钟，取出洗净，烘干； （４）将化学镀银后的基板置于模拟人体体液中，浸泡１０～１２天，取出洗净，烘干，得柔性医用银电极材料。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。