An anode material suitable for high-temperature alkaline storage battery, which is characterized in that the cathode material of the chemical molecular formula: Ni: 1 - A - B - X - Y - Z: Co: a Zn: B Ca: X Mg: y Cu: Z (OH): 2, among them, a, B, x, y and Z respectively represent the number of moles: 0.01 = a = 0.10, 0.005 = b = 0.08, 0.005 = x = 0.08, 0.005 = y = 0.08, z = 0 ~ 0.06. The mixed solution of metal nitrates or mixed metal sulfate solution, Ca (NO: 3): 2 solution, the cathode material and the complexing agent and alkali metal hydroxide solution preparation for high temperature alkaline battery, the invention of the application in high temperature alkaline battery positive pole material can not only meet the normal temperature under alkaline battery the request also has the charge and discharge performance under high temperature, can meet the requirements of Ni MH battery cathode active material.
【技术实现步骤摘要】
本专利技术涉及一种碱性蓄电池(包括Ni/MH、 Ni/Cd、 Ni/Fe、 ,2、 Ni/Zn 电池)正极材料，基本成份为氢氧化镍，Co、 Zn、 Ca、 Mg、 Cu作为惨杂元 素，结构为(3-氢氧化镍，具有适用温度范围宽、高容量和高功率的优点。属 于新能源材料领域。技术背景目前，随着作为新一代高比能绿色镍氢电池在移动通讯、个人电子设备、电 动工具和电动汽车等方面的广泛应用，其正极材料球形氢氧化镍的研究也得到越 来越多地重视，其性能也得到很大的提高。以AA型镍氢电池为例，实际容量已 经从最开始实用化时的1990年每只1070mAh发展到了 2006年的每只超过 2800mAh。但是针对电动工具、动力型氢镍电池(MH/Ni)的正极材料仍存在 诸多不足，主要表现在①掺杂Co、 Zn等的微米级球形Ni(0H)2颗粒，仅考虑细 化微晶晶粒，抑制Y-NiOOH生成，减少镍电极膨胀，却对镍电极反应动力学过程 是不利的，因为Ni(OH)2电极反应是体相氧化一还原反应，H+扩散及电荷迁移"路 径"长、速率慢，电荷传输能力较弱，严重影响活性物质利用率；②大电流充电 时，电子...
【技术保护点】
一种适用于高温碱性蓄电池的正极材料，其特征在于，该正极材料的化学分子式为：Ｎｉ↓［１－ａ－ｂ－ｘ－ｙ－ｚ］Ｃｏ↓［ａ］Ｚｎ↓［ｂ］Ｃａ↓［ｘ］Ｍｇ↓［ｙ］Ｃｕ↓［ｚ］（ＯＨ）↓［２］，其中，ａ、ｂ、ｘ、ｙ、ｚ分别表示摩尔数：０．０１≤ａ≤０．１０，０．００５≤ｂ≤０．０８，０．００５≤ｘ≤０．０８，０．００５≤ｙ≤０．０８，０≤ｚ≤０．０６。
【技术特征摘要】
【专利技术属性】
技术研发人员：傅钟臻，蒋文全，于丽敏，夏雯，
申请(专利权)人：北京有色金属研究总院，
类型：发明
国别省市：11[中国|北京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。