The invention relates to a method of low temperature liquid preparation of CdTe quantum dots include: (1) the CdCl2.2.5H2O and NaOH solution (molar ratio of CdCl2.2.5H2O and NaOH was 1: 2) mixing, adding surfactant and C6H5CH3 C6H5CH3 solution containing Cd2 + A; (2) the Te powder and NaBH4 mixed mixture of deionized water and methanol water solution, B light red NaHTe reaction; (3) the solution mixed with A solution after B, in 60 to 70 DEG C, the reaction time is 18 ~ 20h, which is soluble in organic quantum dots CdTe phase. The method of oil-water interface at low temperature, simple and convenient operation, low temperature, good repeatability, low cost, save for a long time; and the prepared CdTe QDs quantum efficiency can reach 70.2%, narrow size distribution and good monodispersity and other advantages.
【技术实现步骤摘要】
本专利技术属CdTe荧光量子点的制备领域，特别是涉及。
技术介绍
近年来，半导体荧光量子点的研究受到了普遍关注，主要是其独特的发光性能及潜在的应用价值。与传统有机荧光染料相比，半导体量子点呈现出吸收光谱宽而连续，具有良好的发光稳定性，它可以经受反复多次激发而不易发生光漂白。由于这些优异特性，半导体量子点在生物标记、生物检测、生物探针及传感器等领域展示了广泛的应用前景。 目前量子点的合成方法主要可归结为三大类 一种是在高温有机合成法，如CdSe， InAs等，。 此类方法主要优点是得到的荧光纳米材料具有几乎完美的晶体结构及较窄的粒径分布，且分散均匀等；其不利因素是反应时需要在高温条件下进行，且毒性大，并且所用试剂价格昂贵，限制了荧光纳米材料在生物检测、生物标记等领域的应用。另类方法是水相合成法，如利用巯基乙酸做稳定剂来制备CdTe量子点等，。 其优点是成本低、合成方法简单；但此种方法也有明显缺点，如易聚集，分散性差等缺点。第三类方法是反胶束法。此方法制备的纳米粒子小，粒径可控。但此方法制备的量子点易发生粒子团聚。因此，寻求一种制备CdTe量子点的新方法，提高量子点...
【技术保护点】
一种低温液液法制备ＣｄＴｅ荧光量子点的方法，包括： （１）将０．１５Ｍ的ＣｄＣｌ↓［２］.２．５Ｈ↓［２］Ｏ溶液与０．１Ｍ的ＮａＯＨ溶液混合，加入油酸及Ｃ↓［６］Ｈ↓［５］ＣＨ↓［３］，得到含Ｃｄ↑［２＋］的Ｃ↓［６］Ｈ↓［５］ＣＨ↓［３］溶液Ａ，其中，ＣｄＣｌ↓［２］.２．５Ｈ↓［２］Ｏ与ＮａＯＨ的摩尔比为１∶２； （２）将Ｔｅ粉和ＮａＢＨ↓［４］按摩尔比１∶３混合，加入去离子水和甲醇的混合液，反应得到浅红色的ＮａＨＴｅ的水溶液Ｂ，其中，Ｔｅ粉与混合液的比例质量体积比为０．０２～０．０２５ｇ∶１ｍＬ，去离子水与甲醇的体积比为２～２．２∶１； （３）将溶液...
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。