The invention relates to a preparation method of spraying type metal mesh porous material, (1) the iron-based alloy powder, nickel aluminum powder and spray additives mixed evenly; (2) the wire surface cleaning, i.e. derusting, descaling and oil pollution; (3) wire mesh surface treatment. Into the oven preheated temperature control at 70 to 130 DEG C; (4) by oxygen acetylene flame spraying powder base, bottom form a pore on the surface of metal mesh; (5) using mixed powder spraying oxygen acetylene flame spray gun, the formation of porous structure by spraying type metal mesh porous material. The invention has the advantages of simple process, low cost and high efficiency, and can meet the requirements of industrialized application.
【技术实现步骤摘要】
本专利技术涉及金属多孔材料
，具体地说，是。
技术介绍
金属多孔材料是由连续的刚性骨架和孔隙所组成，具有优异的物理特性和良好的机械性能，兼具功能和结构双重用途。由于丰富的孔隙结构形态、较大的孔率范围，其已经广泛应用于航空航天、电子与通信、电化学、石油化工、交通运输、冶金、机械、医学、环保、建筑等各种领域，涉及流体分离过滤、流体渗透与分布控制、消音降噪、电磁屏蔽、隔热阻火、高效燃烧、强化传质传热、阻燃防爆、电化学过程、催化反应工程和生物工程等诸多方面，可制作过滤器、流体分离器、催化剂及催化剂载体、隔声材料、消声器、电磁屏蔽器件、阻燃器、换热器、散热器、多孔电极等，是国民经济发展不可缺少的关键材料。目前金属多孔材料的制备方法主要有以下几种粉末烧结法据CN101260483，其制备方法是①将一定粒度的Ni粉、Al粉和NaCl粉按重量百分比均匀混合；②采用模压或冷等静压成形；③先《氏温烧结，再中温脱除造孔剂，最后，再高温烧结，使金属间化合物完全形成Ni3Al相，得到镍铝基合金多孔材料；此专利技术优点是孔隙分布均匀，孔隙大小 可控，孔隙度可自由调节，其缺点是工序多、...
【技术保护点】
一种喷涂型金属丝网多孔材料的制备方法，其特征在于，具体步骤为： （１）将铁基合金粉末、镍包铝粉末与喷涂助剂混合均匀； （２）对金属丝网进行表面清洁处理，即除锈、去除氧化皮及油污； （３）将表面处理好的金属丝网放入恒温箱中进行预热，温度控制在７０～１３０℃； （４）采用氧－乙炔火焰喷枪喷涂打底粉，在金属丝网表面形成底层； （５）采用氧－乙炔火焰喷枪喷涂混合粉末，形成多孔结构，得到喷涂型金属丝网多孔材料。
【技术特征摘要】
【专利技术属性】
技术研发人员：徐宏，曾勇，侯峰，戴玉林，杨胜，王宏智，
申请(专利权)人：华东理工大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。