Electron beam irradiation, the invention relates to a synthesis method of nanometer zinc selenide quantum dot powder, a nano inorganic compound semiconductor material preparation technology field. The invention adopts six hydrated zinc nitrate and sodium selenite as raw materials, the molar concentration of both solution ratio of 1: 1 to 1: 2; chelating agent ethylenediaminetetraacetic acid two sodium and oxidative free radical scavenger OH. isopropanol; stirring to mix evenly; and then the mixture is placed in a sealed container and set in 2.5MeV, 6 ~ electron beam irradiation electron accelerator 7mA production under irradiation treatment, the irradiation dose of 14 ~ 42Mrad, irradiation time is 10 ~ 30 minutes; finally the reaction product rotation after irradiation of steam condensed, dialysis, and high speed centrifuge separation; by ethanol washing times, vacuum drying, finally obtained ZnSe quantum dots powder white body. The method has the advantages of simple and convenient method, fast synthesis, good safety, no pollution and favorable environment protection.
【技术实现步骤摘要】
一种，属纳米无机化合物半导体材料制备 工艺
技术介绍
ZnSe是一种性能良好的II-VI族半导体发材料，具有直接跃迁型能带结构，室温下禁带 宽度为2.67eV。具有宽的透光范围(0.5 22.0pm)，较高的发光效率，低的吸收比。近年来， ZnSe在光致发光和电致发光器件，激光器和薄膜太阳能电池等材料上有广泛的应用。基于ZnSe材料的广泛应用，科学工作者已经发展了各种用于制备ZnSe材料的方法，包 括升华法、化学气相沉积法(CVD)、分子束外延法(MBE)、溶剂热法以及水热法等。Peng等 人在水热条件下用单质锌粉和单质硒粉在18(TC保温24小时条件下得到了立方相ZnSe纳米 颗粒，其平均尺寸为70 100nra。传统制备ZnSe的方法具有工艺复杂，制备时间长，需要高温高压，所用原料有毒等缺点。 用电子束辐照技术制备纳米材料是一种新颖的方法，其制备过程简单、快速，所需原料低毒 易得，产物性能良好，是一种绿色高效的合成方法。
技术实现思路
本专利技术的目的是提供一种。 本专利技术一种，其特征在于具有以下的过程和步骤a. 首先用电子天平称取一定量的六水合...
【技术保护点】
一种纳米硒化锌量子点粉体的电子束辐照合成方法，其特征在于具有以下的过程和步骤： ａ．首先用电子天平称取一定量的六水合硝酸锌和作为螯合剂的乙二胺四乙酸二钠（ＥＤＴＡ），将其溶于蒸馏水中，使其中的锌离子与ＥＤＴＡ的摩尔浓度比为１∶４～１∶６；搅拌使混合均匀；然后加入亚硒酸钠，使其与锌离子的摩尔浓度比为１∶１～２∶１；搅拌混合，制成无色透明的溶胶；然后用１ｍｏｌ／Ｌ的ＮａＯＨ溶液调节ｐＨ值为９～１０；然后再加入作为氧化性自由基ＯＨ.清除剂的异丙醇，异丙醇的加入量以含有上述各物质的混合溶液的量为计量基准，其体积含量比为６～１０ｍｌ／１００ｍｌ，即每１００ｍｌ混合溶液需加入６～１０...
【技术特征摘要】
【专利技术属性】
技术研发人员：李珍，刘岩岩，方耀国，吴明红，潘登余，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。