The invention relates to a control method for cutting length of a metal powder rolling raw slab, belonging to the technical field of metal powder rolling technology. The present invention utilizes traditional conventional rolling equipment to improve and assemble, and obtains rolling equipment with rolling pressure electronic sensing system device. The invention utilizes the electric pressure sensing system device, force pressure measurement of metal powder rolling machine in the rolling process, the rolling process and by recording the pressure variation trend or curve, was rolling pressure to be stable through time, the time to take the roller rotating speed can be obtained by metal powder rolling slab cutting head length of life. The method has the advantages of energy saving, energy saving and raw material, and is favorable for improving the quality of products. The method of the invention can realize the objective and scientific evaluation of the length of the cutting head in the technological process, and is beneficial to realize the optimization of the process.
【技术实现步骤摘要】
本专利技术涉及一种，属金属粉末轧制工艺
技术介绍
现有粉末轧制生板坯切头工艺方法是将金属粉末通过喂料漏斗送入粉末轧机轧制，轧 制坯料的前端密度明显低于其它部位。根据所用材料的不同，两者相差25~35%不等，为了保 证产品质量，需要将其切除。目前，生板坯切头长度主要由技术人员凭经验来确定。从上述的分析可知目前生板坯切头长度的确定过程经验性和主观性占主导地位，工艺 的制定尚缺乏一种客观的依据。主要弊端表现为切头过长，会造成原料的浪费；切头过短， 又会造成烧结产品质量下降和烧结能源的浪费。造成现有技术存在以上缺陷的主要原因是缺乏一种客观量化指标评价轧制工艺的合理 性。具体而言，即粉末轧制生板坯切头长度的确定尚缺乏一种精确的方法。因此，如何采用 适当的方法确定生板坯切头长度，是解决目前工艺缺陷与不足的核心问题。
技术实现思路
本专利技术的目的是解决上述的缺陷和不足，提供一种金属粉末轧制生板坯切头长度的控制 方。本专利技术采用了采集轧制压力变化趋势的方法来确定金属粉末轧制生板坯切头的长度。本专利技术一种，其特征在于具有以下的过程和步 骤将金属或合金粉末放置特制的带...
【技术保护点】
一种金属粉末轧制生板坯切头长度的控制方法，其特征在于具有以下的过程和步骤：将金属或合金粉末放置特制的带有轧制压力电子传感器系统装置的轧制设备的两个轧辊之间，然后启动电机，使一对轧辊在一定转速下相对转动，并使位于两轧辊间隙中的金属或合金粉末经受一定压力的挤压或轧制；起始时压力是不稳定的，当轧制压力趋于稳定时，轧制坯料的密度也将趋于稳定；通过特制设备的压力电子传感系统所记录的压力随时间的变化趋势或变化曲线，可以确定生板坯初期所产生的切头长度，也即是说，通过轧制压力达到稳定所经历的时间乘以轧辊转动速度，即可求得生板坯切头长度。
【技术特征摘要】
【专利技术属性】
技术研发人员：杨宁，朱玉斌，孙远，许伟，王妍，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。