The invention relates to a method for preparing titanium dioxide / multi wall carbon nanotube composite photocatalyst by electron beam irradiation, belonging to the field of radiation chemistry and preparation process of photocatalyst. The method of the invention is the preparation process of multiwalled carbon nanotubes (MWCNTs) into titanium tetrafluoride (TiF4) solution, and ultrasonic dispersion, make fully mixed; the mass ratio is MWCNTs:TiF4 = 0.05 ~ 0.15; irradiation and the solution is then placed in the electronic accelerator under irradiation treatment; irradiation dose of 280 ~ 560KYy; and then moved to another container, seal into the oven, at 60 DEG C for 20 hours; and then the product is washed and dried, finally prepared TiO2 / MWCNTs composite photocatalyst. The composite photocatalyst obtained by the method of the invention has good photocatalytic performance and has better photocatalytic effect.
【技术实现步骤摘要】
本专利技术涉及一种，属于辐射 化学及光催化剂制备工艺
技术介绍
展望21世纪，人类在充分享受现代文明的同时，也面临着资源短缺、环境污染以及自然 生态危机等一系列的世界性难题。如何合理开发和利用资源，以及如何保护好环境已是实现 人类可持续发展的关键意义所在。目前，随着空气、水体污染的不断加剧，环境污染治理巳 成为人类社会面临和亟待解决的重大课题。自从1972年日本Fujishima发现Ti02单晶电极光催化分解水以来，光催化技术得到了广泛 的关注，光催化技术有可能解决人类未来的环境污染问题。光催化技术在常温、常压下就可 以进行，能够彻底破坏有机或无机污染物，并使之完全、快速氧化为C02、仏0等无害物质，避 免了二次污染，从而达到净化环境的目的。目前，在众多的半导体光催化剂中，Ti02因其无 毒，比表面积大，表面活性高，且具有较高的热稳定性、化学稳定性等特点而被认为是比较 理想的光催化剂之一。但Ti02的禁带宽度大于3.0 eV，可见光区的量子效率低，光生载流子 (电子和空穴)的复合率较高，导致量子限域率降低，影响催化效率，严重制约了Ti02的实 际应用...
【技术保护点】
一种电子束辐照制备二氧化钛／多壁碳纳米管复合光催化剂的方法，其特征在于具有以下的过程和步骤：ａ．称取一定量的多壁碳纳米管（ＭＷＣＮＴｓ）加入到一定浓度的四氟化钛（ＦｉＦ４）溶液中，并用超声波分散３０分钟，使其充分混合均匀；多壁碳纳米管与四氟化钛两者的质量比即ＭＷＣＮＴｓ∶ＴｉＦ↓［４］＝０．０５～０．１５；ｂ．将超声处理后的上述溶液倒入封口的聚乙烯塑料密封袋中，将其放在电子加速器下的辐照区进行辐照处理，辐照剂量为２８０～５６０ＫＧｙ；ｃ．将经辐照后的溶液转移至另一容器中，用封口膜封口后放入烘箱内，于６０℃下反应２０小时；ｄ．然后取出容器，依次用去离子水和乙醇洗涤反应产物；ｅ...
【技术特征摘要】
【专利技术属性】
技术研发人员：焦正，张海娇，郭会娇，徐盼盼，吴若飞，李智勇，王琳，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。