The invention discloses an epoxy matrix resin with high heat resistance and toughness and a preparation method and an application thereof. The epoxy resin matrix is composed of the following ingredients: 100 parts by weight of epoxy resin, curing agent 20 to 60 parts by weight of 0.5 to 5, the curing accelerator mass of a and 5 to 50 parts by weight of a thermoplastic resin; glass transition temperature of the epoxy resin matrix for 210 - 235 DEG C, the tensile strength is 8086MPa for 3.0%3.3%, elongation, tensile modulus of elasticity for 3.23.5GPa. The epoxy matrix resin provided by the invention can meet the carbon fiber prepreg solvent process and hot melt impregnation process requirements, by a proper process after curing, curing material has excellent comprehensive properties, especially with high heat resistance and high toughness characteristics, can be used for the preparation of high performance composite material in aerospace, aviation, the field of high technology to meet the aerospace to represent the needs of the.
【技术实现步骤摘要】
本专利技术涉及一种高耐热高韧性的环氧基体树脂及其制备方法与应用。
技术介绍
环氧树脂具有较好的耐热性、力学性能及工艺性等优点，已经在许多领域得到 广泛应用，目前是碳纤维复合材料最常用的基体树脂之一。碳/环氧复合材料具有比 强度和比模量高、可设计性好、抗疲劳性好、结构尺寸稳定性好以及便于大面积整 体成型的独特优点在航天航空领域得到了广泛的应用。但是环氧树脂在固化后存在 韧性不足的缺点，不能有效发挥碳纤维的性能，其碳纤维复合材料在承受载荷时往 往由于环氧树脂的过早失效导致复合材料的破坏。为了适应高性能碳纤维复合材料 对基体树脂的需求，环氧树脂的改性一直是相关领域的研究热点，兼具韧性、强度、 耐热性和优良加工性能的环氧树脂一直是环氧树脂改性的发展方向。环氧树脂的改性方法有很多，从添加第二相的方向来说，常见的有橡胶弹性体 改性环氧树脂，纳米粒子改性环氧树脂，超支化聚合物改性环氧树脂以及热塑性树 脂改性环氧树脂等；而从环氧树脂自身的分子链结构来说，主要是从环氧树脂和固 化剂分子结构来进行改性。在这些改性方法中，单一的改性方法往往具有一定的局 限性，比如橡胶弹性体改性环氧...
【技术保护点】
一种环氧基体树脂，由下述成分制成：１００质量份的环氧树脂，２０－６０质量份的固化剂，０．５－５．０质量份的固化促进剂和５－５０质量份的热塑性树脂；所述环氧基体树脂的玻璃化温度为２１０－２３５℃，拉伸强度为８０－８６ＭＰａ，断裂延伸率为３．０％－３．３％，拉伸弹性模量为３．２－３．５ＧＰａ。
【技术特征摘要】
【专利技术属性】
技术研发人员：杨士勇，陈伟明，陶志强，
申请(专利权)人：中国科学院化学研究所，
类型：发明