The invention relates to a preparation method of modified polyurethane paint based on carrier control technology. This method is a mineral salt MgCO3, CaSO4 or BaSO4 in the ground into powder, and then prepared into suspension, regulating the pH value to 7 ~ 8.5, filtration and drying of nanometer powder; three EPDM coating, nano powder and three EPDM mass ratio of 1: 2 to 5; the quality of nano powder and polyurethane paint is 1: 2 ~ 6 were mixed and milled for 24 ~ 40 hours. The modified S01 varnish, S22 - 3 - 1 and 7110J - 6 double component polyurethane paint type polyurethane paint and polyurethane paint before by calculating the carrier density shows that the modified polyurethane paint when insulation performance is improved greatly. This makes polyurethane paint not only applicable to the surface coating of high-grade furniture and civil wooden furniture, but also can be applied to the anti-corrosion coating of mechanical equipment, chemical equipment and cement construction.
【技术实现步骤摘要】
本专利技术涉及有机涂料
，是一种基于载流子控制技术制备改性聚氨酯漆制备方法。
技术介绍
聚氨酯类涂料是现代涂料工业的重要品种，据不完全统计，当前我国涂料总产量超过了 200万吨，聚氨酯涂料所占的比例从2001年的22万吨，增长到2009年占涂料总产量的21%, 达到41万吨，是近十年来增长速度最快的涂料品种，预计今后五年仍将以每年5%左右的速 度递增。究其原因，主要有以下三个方面 一是由于国民经济的发展，人民生活水平的提高， 涂料市场对高档漆的需求增加，多年研究开发的聚氨酯涂料已形成系列，使用范围不断扩展， 从而使聚氨酯涂料的市场容量迅速扩大；二是由于聚氨酯漆具有良好的装饰性、耐久性和耐 腐蚀性，能适应木器家具、家居木结构装修、地板地坪耐磨防蚀、体育场馆和运动器材等涂 饰的各种要求，得到了消费者的青睐；三是由于生产聚氨酯涂料的重要原料TDI，价格降低， 供应有保证，从过去单纯依靠进口，经过引进、消化、吸收，在国内已陆续投产。聚氨酯漆由于大气、紫外线、污染物等环境因素的影响，其本身的物理和化学性质会逐 渐失效，特别是绝缘性能会急剧下降,这严重影响了聚氨酯漆...
【技术保护点】
一种基于载流子控制技术的改性聚氨酯漆的制备方法，其特征在于该方法具有以下步骤： １）采用高速球磨机将成份为ＭｇＣＯ↓［３］、ＣａＳＯ↓［４］或ＢａＳＯ↓［４］其中之一的矿物盐研磨成纳米粉体，粒径保持在５０～２００ｎｍ范围内，然后将纳米粉体配制成２０～４０％（ｗｔ％）的悬浮液，同时调节ｐＨ值为７．０～８．５，进行抽滤，接着将所得滤饼在１２０～２００℃下烘干，直到滤饼变为干燥的白色细晶态物质，即得纳米粉体； ２）对步骤１所得的纳米粉体进行包覆处理，以三元乙丙橡胶作为包覆剂，其中纳米粉体与三元乙丙橡胶的质量比１∶２～５； ３）将步骤２所得的纳米粉体与聚氨酯漆混合，纳米粉体与...
【技术特征摘要】
【专利技术属性】
技术研发人员：钟庆东，林海，王超，盛敏奇，陈大洋，周琼宇，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。