The invention relates to a preparation method of modified two-component polyurethane paint based on carrier control technology. The preparation of modified polyurethane paint is controlled by the carrier control technology by modifying the raw material polyisocyanate with nanometer powder. This method is a mineral salt CaCO3, MgSO4 or BaSO4 in the ground into powder, and then prepared into suspension, while the pH value is adjusted to 7 to 8, standing, filtering and drying; the nanometer powder three EPDM coating, nano powder and three yuan of ethylene propylene rubber the mass ratio of 1: 2 to 5; the quality of nano powder and polyurethane paint is 1: 5 ~ 7 were mixed and milled for 30 ~ 40 hours. Modified polyurethane paint of the invention, after testing and trial proved that the coating adhesion, good gloss, high hardness, wear resistance, temperature resistance, water resistance, chemical corrosion, construction and leveling performance, climate adaptability, convenient use, low cost.
【技术实现步骤摘要】
本专利技术涉及聚氨酯漆
，是一种基于载流子控制技术制备改性双组分聚氨酯漆的方法。
技术介绍
聚氨酯类涂料是现代涂料工业的重要品种，据不完全统计，当前我国涂料总产量 超过了 200万吨，聚氨酯涂料所占的比例从2001年的22万吨，增长到2009年占涂料总产 量的21%，达到41万吨，是近十年来增长速度最快的涂料品种，预计今后五年仍将以每年 5%左右的速度递增。究其原因，主要有以下三个方面一是由于国民经济的发展，人民生活 水平的提高，涂料市场对高档漆的需求增加，多年研究开发的聚氨酯涂料已形成系列，使用 范围不断扩展，从而使聚氨酯涂料的市场容量迅速扩大；二是由于聚氨酯漆具有良好的装 饰性、耐久性和耐腐蚀性，能适应木器家具、家居木结构装修、地板地坪耐磨防蚀、体育场馆 和运动器材等涂饰的各种要求，得到了消费者的青睐；三是由于生产聚氨酯涂料的重要原 料TDI，价格降低，供应有保证，从过去单纯依靠进口，经过引进、消化、吸收，在国内已陆续 投产。 聚氨酯漆的常规制备方法是以邻苯二甲酸酐、己二酸、i^一烯酸、顺酐、丙二醇及 三羟甲基丙烷等原料合成，这些原料均为紧俏价高的化...
【技术保护点】
一种基于载流子控制技术的改性双组分聚氨酯漆的制备方法，其特征在于其具体的操作步骤如下： １）甲组份按配料比将己二酸、苯酐、三羟甲基丙烷同时加入反应釜中，缓缓升温至２１０℃，加入脱水剂，保温酯化，当羟值达到３～６％时，降温至１２０℃，兑稀，再降温至５０℃以下，过滤即为甲组份成品；其中甲组份中各原料配比为：己二酸３７ｇ，苯酐３１．２ｇ，三羟甲基丙烷５０．５ｇ； ２）采用高速球磨机将成份为ＣａＣＯ↓［３］、ＭｇＳＯ↓［４］或ＢａＳＯ↓［４］其中之一的矿物盐研磨成纳米粉体，粒径保持在１０～１００ｎｍ范围内，然后将纳米粉体配制成２０～３０％（ｗｔ％）的悬浮液，同时调节ｐＨ值为７．...
【技术特征摘要】
【专利技术属性】
技术研发人员：钟庆东，林海，王超，盛敏奇，周琼宇，陈大洋，
申请(专利权)人：上海大学，
类型：发明
国别省市：31[]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。