The invention relates to an anti adhesion linear low density polyethylene composition, the composition is LLDPE as the base material, including anti adhesion agent, dispersant, antioxidant; anti adhesion agent LLDPE weight 0.1 ~ 0.15%, dispersant is 0.05 ~ LLDPE, the weight of 0.1% antioxidants was 0.01 LLDPE ~ 0.03% weight, anti the adhesion agent is stearic acid amide and sodium hydrogen phosphate, two weight ratio of 3: 1 to 4: 1, dispersant for zinc stearate and antioxidant as beta (3 ', 5' - 4 '- Di tert butyl eighteen hydroxyphenyl) acrylic ester; the LLDPE composition and effect of anti adhesion to do not damage the linear low density polyethylene film transparency, gloss, color or appearance, will not adversely affect the mechanical properties It can obviously improve the opening property of the linear low density polyethylene film, and the process is simple and easy.
【技术实现步骤摘要】
本专利技术涉及一种防粘连线性低密度聚乙烯组合物。
技术介绍
线性低密度聚乙烯(LLDPE)的加工性、光泽度好于高密度聚乙 烯，抗撕裂强度、拉伸强度和耐环境应力开裂性等比低密度聚乙烯要 好，因此，LLDPE在薄膜制造上有很大的优势。线性低密度聚乙烯薄膜广泛地应用于食品包装、医药包装、文化 用品包装、工业品包装及农用薄膜等方面。但是在吹塑成膜过程中， 由于具有很高的磨擦系数，使得它们有自行黏附和附着在金属表面上 的倾向，进行挤出时，将会表现出黏性。由于巻曲易粘在一起，开口 困难，并且还能黏附到轧辊上，毁坏模板框，从而导致产品起皱和无 法使用。这些问题会降低生产率，使生产的废料量增加，降低线性低 密度聚乙烯薄膜产量，同时由于薄膜和设备之间的磨擦会产生静电， 造成巻曲过程中磨擦太大，从而影响线性低密度聚乙烯薄膜的光亮 度。为了解决线性低密度聚乙烯薄膜的粘连现象，人们在聚乙烯薄膜 的制造过程中加入防粘连剂(或称开口剂)。使用最多的防粘连剂是 硅类添加剂，在线性低密度聚乙烯树脂从模头挤出之后，此种硅类添 加剂中的一部分将会突出于线性低密度聚乙烯薄膜表面之处并夹藏空气，解决...
【技术保护点】
一种防粘连线性低密度聚乙烯组合物，其特征在于：其组成是：以线性低密度聚乙烯为基料，包含有防粘连剂、分散剂、抗氧剂；其中防粘连剂为线性低密度聚乙烯重量的０．１～０．１５％、分散剂为线性低密度聚乙烯重量的０．０５～０．１％、抗氧剂为线性低密度聚乙烯重量的０．０１～０．０３％； 防粘连剂为硬脂酸酰胺和磷酸氢钠，二者重量比为３∶１～４∶１； 磷酸氢钠的粒径为１０μｍ～２０μｍ； 分散剂为硬脂酸锌； 抗氧剂为β－（３’，５’－二叔丁基－４’－羟基苯基）丙烯十八酯 。
【技术特征摘要】
【专利技术属性】
技术研发人员：张剑，刘聪，陈光岩，张欣颖，王安晨，澎洪湃，
申请(专利权)人：中国石油天然气股份有限公司，
类型：发明
国别省市：11[中国|北京]