一种水热法制备纳米氧化锌的方法技术

本发明专利技术是一种水热法制备纳米氧化锌的方法。其主要内容是以锌盐、氨水为原料，聚丙烯酸盐为分散控制剂，水为溶剂，在１００～１２０℃的温度下常压反应１５小时，得到平均粒径在８７～４６０纳米之间、能稳定分散在水溶液中的氧化锌／聚丙烯酸盐复合纳米粒子，其中粒径为２～５纳米的纳米氧化锌粒子被聚丙烯酸盐分子链包裹着。其特点在于工艺简单，制备成本低，氧化锌粒子粒径小、均一性好且能以复合粒子的形式稳定分散在水溶液中。

Method for preparing nano Zinc Oxide by hydrothermal method

The invention relates to a method for preparing nanometer Zinc Oxide by hydrothermal method. The main content of which is the zinc salt and ammonia as raw materials, polyacrylate dispersing control agent, water as solvent, at 100 to 120 DEG C under atmospheric pressure reaction for 15 hours, average grain size is 87 ~ 460 nm and the dispersion in aqueous solution of Zinc Oxide / polyacrylate composite nanoparticles. The particle size of 2 to 5 nm by Zinc Oxide nano particle polyacrylate molecular chain wrapped. The utility model is characterized in that the process is simple, the preparation cost is low, the particle size of the Zinc Oxide particle is small, the homogeneity is good, and the powder can be stably dispersed in the aqueous solution in the form of composite particles.

【技术实现步骤摘要】

【技术保护点】
一种水热法制备纳米氧化锌的方法，其特征在于包括以下步骤：首先将锌盐、氨水、聚丙烯酸盐和水配置成溶液，其中以整个溶液质量百分比计，锌盐占１．００ｗｔ％，氨水占２．６０ｗｔ％，聚丙烯酸盐含量在０．７５～２．５０ｗｔ％之间；然后将配制所得溶液在１００～１２０℃的温度下常压反应１５小时，得到平均粒径在８７～４６０纳米之间、能稳定分散在水溶液中的氧化锌／聚丙烯酸盐复合纳米粒子，其中的纳米氧化锌粒子的粒径在２～５纳米之间，被聚丙烯酸盐分子链包裹着。

【技术特征摘要】

【专利技术属性】
技术研发人员：赵京波，肖鑫，杨万泰，
申请(专利权)人：北京化工大学，
类型：发明
国别省市：11[中国|北京]