The invention discloses a metal supported gold catalyst and preparation of aldehydes or ketones in the catalyst for selective oxidation of alcohols, the catalyst is the metal fibers or metal particle carrier with chloroauric acid or sodium tetrachloroaurate solution Impregnation after calcination at 250~400 DEG C for 2 hours, the weight of gold catalyst from 0.5 to 6%, with carrier weight of 94 to 99.5%; the process of oxidative dehydrogenation of aldehydes or ketones in the catalyst catalyzed gas phase selectivity, using a fixed bed reactor with oxygen or air as oxidant, the reaction temperature is 250~350 DEG C, alcohol weight hourly space for 10~60 hours, up to 1 O, down 2 / hydroxyl molar ratio of between 0.4 and 1.2, the alcohol selective oxidation of the aldehyde or ketone. The catalyst has the advantages of good thermal conductivity, low temperature activity, high selectivity, good stability and low cost. The catalyst has high efficiency and environmental friendliness in the preparation of aldehydes or ketones by selective oxidation and dehydrogenation of alcohols.
【技术实现步骤摘要】
本专利技术属于催化
，具体地说是一种以金属为载体负载金催化剂 及其该催化剂在催化醇气相选择性氧化脱氢制备醛或酮中的应用。
技术介绍
金一直被认为是化学惰性金属，相对于铂、钯等其它贵金属，金的催化潜力一直未能引起足够的重视。20世纪80年代，日本科学家Hamta和英国 科学家Hutchings等人发现纳米金颗粒拥有非凡的催 化作用。目前，Au催化剂在CO低温氧化、选择性加氢、NOx还原生成N2和 醇选择性氧化脱氢等反应中表现出了优异的催化性能，不仅反应条件温和、 活性和选择性高、稳定性好，而且具有良好的抗水性、稳定性和湿度增强效 应。因此，金催化剂由于其优异的催化性能，在众多领域展示出巨大的应用 潜力。醛或酮的制备是有机合成和精细化工的重要反应， 一般是在有机溶剂存 在下，用化学计量的有毒重金属盐氧化剂(如Cr盐)氧化醇的方法来制备。 也有醛或酮(如苯甲醛)可以通过有机卤代物的水解来制备。上述过程均存 在严重的污染和产品有毒组分残留等问题。醇的选择性氧化脱氢过程，由于 不采用有机溶剂、不采用有毒有害的氧化剂、可以避免产物中有毒物(如有 机氯代物)的残余，而...
【技术保护点】
一种金属载体负载金催化剂，其特征在于该催化剂是将金属纤维或金属颗粒载体用含金为２～１０克／升的氯金酸或氯金酸钠溶液等体积浸渍后，于２５０～４００℃焙烧２小时制得，所得催化剂含金重量为０．５－６．０％、含载体重量为９４．０－９９．５％；所用金属纤维或金属颗粒载体的材质是镍、不锈钢、钛、铝、锌、紫铜或黄铜；金属纤维直径２～１５０微米，长度２～１０毫米；金属颗粒大小为０．１～１．０毫米。
【技术特征摘要】
【专利技术属性】
技术研发人员：路勇，赵国锋，邓苗苗，薛青松，刘晔，何鸣元，
申请(专利权)人：华东师范大学，
类型：发明
国别省市：31[]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。