The invention discloses a rare earth containing yttrium with high strength and high damping magnesium alloy, which is characterized in that the magnesium alloy is composed of Mg, Al, Zn, Y and Mn, the components by weight percent: Al:2.9% ~ 3.1%; Zn:0.9% ~ 1.1%; Y:0.5% ~ 2%; Mn:0.29% ~ 0.31%, the remaining impurities Mg and inevitable. The invention can make high strength AZ deformation mechanical properties and damping properties of magnesium alloy are greatly improved, successfully solve the contradiction between the mechanical properties and damping capacity of magnesium alloy, can meet the actual needs of the high-speed train, automobile, aerospace and defense industry and other fields of high strength and high damping lightweight materials. Moreover, the cost of the magnesium alloy material used in the invention is low, and the process equipment is a general and general equipment, which has the advantages of strong portability and easy operation.
【技术实现步骤摘要】
本专利技术涉及一种合金材料，特别涉及一种添加稀土钇以提高合金强度和阻 尼的镁合金材料。
技术介绍
近年来，随着汽车工业、轨道交通、以及飞行器日趋轻量化、高速化和大 功率化，对降低产品自重，提高便携性，降低能源消耗和减振降噪性等都提出 了更迫切的要求。而传统的钢铁材料已经渐渐不能满足其需求，由此急需寻求 一种密度小、强度高、阻尼性能好的金属结构材料。在众多金属结构材料中，纯镁具有密度低、阻尼减振降噪能力强、比强度 高、电磁屏蔽性能好等一系列优点，引起了人们的广泛研究。但纯镁力学性能较差，大大限制了其应用范围。 一些镁合金虽然具有较高的强度，如AZ系、ZK 系等镁合金，可以运用到工业生产，但其强化方式主要为固溶强化、细晶强化 等，这些固溶进去的溶质原子和密集的晶界作为镁基面滑移位错的强钉扎点， 导致阻尼性能大大降低，因而不能解决高速化和大功率化后所引起的振动和噪 声问题。随着镁合金研究的发展以及应用领域的拓展，解决高强度AZ系、ZK系 等变形镁合金力学性能和阻尼性能之间的矛盾，开发同时具有高阻尼和优良力 学性能的镁基材料成为了一个急待解决的重要问题。现在一般的思路是...
【技术保护点】
一种含稀土钇的高强度高阻尼变形镁合金，其特征在于，所述镁合金由Ｍｇ、Ａｌ、Ｚｎ、Ｙ、Ｍｎ组成，各组成成分质量百分含量为：Ａｌ：２．９％～３．１％；Ｚｎ：０．９％～１．１％；Ｙ：０．５％～２％；Ｍｎ：０．２９％～０．３１％，其余为Ｍｇ和不可避免的杂质。
【技术特征摘要】
1、一种含稀土钇的高强度高阻尼变形镁合金，其特征在于，所述镁合金由Mg、Al、Zn、Y、Mn组成，各组成成分质量百分含量为Al2.9％～3.1％；Zn0.9％～1.1％；Y0.5％～2％；Mn0.29％～0.31％，其余为M...
【专利技术属性】
技术研发人员：王敬丰，潘复生，赵亮，高珊，
申请(专利权)人：重庆大学，
类型：发明
国别省市：85[]