The invention relates to a preparation method of a sea urchin chain manganese dioxide absorber particle, belonging to the cross technical field of material science and chemical synthesis. Method for preparing sea urchin chain manganese dioxide absorber particles. The utility model is characterized in that a manganese dioxide absorber particle with chain shape of sea urchin is prepared by chemical method under the action of an external magnetic field. The effect and the advantage of the invention are that the magnetic structure of the sea urchin can be effectively prepared by strengthening the magnetic field through the external strengthening magnetic field, and the magnetic loss performance of the manganese dioxide is improved. In addition, the preparation method is simple, low cost, stable performance, and has a good application prospect.
【技术实现步骤摘要】
本专利技术属于材料科学和化学合成制备的交叉
，涉及新型吸收剂颗粒的制备技术。特别涉及到一种海胆链状二氧化锰颗粒的制备方法。
技术介绍
随着对电磁波吸收材料研究的深入以及实际应用的需求，高吸收性能、宽频 段、重量轻、体积小等高性能吸波材料已成为当前的研究重点。吸收剂作为吸波材料的 核心，在电磁波吸收材料中发挥着重要作用。然而，传统的是以石墨、铁氧体、炭黑等 为代表的一类吸收剂，由于吸收频带窄和密度大等缺点而限制了其应用。相反，新型吸 收剂是在充分研究传统吸收剂的基础之上，结合现代先进的科学技术手段制备而成，具 有轻、宽、强等传统吸收剂所不具备的优点。二氧化锰是一种具有重要工业用途 的氧化物，其离子交换性能、分子吸附性能、电化学性能和电磁波吸收性能，使其在催 化、电极以及吸波材料等领域展现出优越的实用价值和商业价值。特别是二氧化锰具有 多样的晶体结构和形貌特征等优点，可以通过控制形貌等手段来提高其电磁性能。
技术实现思路
本专利技术要解决的技术问题是提供一种在外场作用下用化学法制备海胆链状二氧 化锰吸收剂颗粒，使其电磁波磁损耗性能得到有效提高。 本专利技术的...
【技术保护点】
一种海胆链状二氧化锰吸收剂颗粒的制备方法，其特征在于该方法的具体步骤为：将硫酸锰和过硫酸铵按摩尔比为２∶５－７用蒸馏水进行稀释搅拌均匀；随后放入磁场中并立即开启磁场和加热装置，磁场强度为１Ｔ－１０Ｔ，反应温度控制在７０℃，反应时间控制４小时；反应完成后将反应产物分别用酒精和蒸馏水洗涤多次，最后置于真空干燥箱中在６０℃－８０℃下干燥２４小时，得到海胆链状二氧化锰粉末。
【技术特征摘要】
一种海胆链状二氧化锰吸收剂颗粒的制备方法，其特征在于该方法的具体步骤为将硫酸锰和过硫酸铵按摩尔比为2∶5-7用蒸馏水进行稀释搅拌均匀；随后放入磁场中并立即开启磁场和加热装置，磁场强度为1T-10T，反应温度控制在70℃，反应时间控制4小时；反应完成后将反应产物分别...
【专利技术属性】
技术研发人员：段玉平，张佳，刘顺华，
申请(专利权)人：大连理工大学，
类型：发明
国别省市：91[中国|大连]