The invention discloses a preparation method and application of vinyl chloride polymer, which relates to the technical field of vinyl chloride, including the following steps: placing vinyl chloride and anti adhesive agent in the reactor, vacuuming the reactor to a pressure of \uffe3 0.1 \uffe3 0.05 MPa, then injecting chlorine gas into the reactor with a pressure of 0.2-0.6 MPa to carry out chlorination reaction. After the reaction, the waste gas is discharged and repeated The chlorinated polyvinyl chloride (CPVC) is obtained by vacuumizing, chlorinating and exhausting waste gas. The preparation method of vinyl chloride polymer, the method for preparing vinyl chloride polymer by bulk polymerization and the vinyl chloride polymer prepared thereby can be easily applied to industries requiring vinyl chloride polymer, such as the industry involving vinyl chloride resin and its molded products.
【技术实现步骤摘要】
一种氯乙烯聚合物的制备方法及应用
本专利技术涉及氯乙烯
，具体地说，本专利技术涉及氯乙烯聚合物的制备方法及应用。
技术介绍
氯乙烯聚合物是包含50％以上的氯乙烯的聚合物，其价廉，易于控制硬度，适用于大部分加工设备并且具有多种应用领域。此外，氯乙烯聚合物可以提供具有优良的物理和化学性能例如机械强度、耐候性和耐化学性的模塑产品，并且广泛地用于各种领域。但是，氯乙烯聚合物由于在加工过程中施加的热或紫外线，在聚合反应过程中产生的化学结构的缺陷引起脱氯化氢作用，因此会引起树脂的变色或物理性能的劣化。具体地，在氯乙烯聚合物中，存在聚合反应中产生的化学缺陷，即氯丙烯和三氯化物化学结构的缺陷。由于所述化学结构的缺陷，氯乙烯聚合物中的碳与氯的结合能会比通常分子结构中的碳与氯的结合能低得多，而且由于在氯乙烯聚合物的加工过程中的外部自由基转移，碳与氯之间的键合会容易地破坏。来自聚合物链的单独的氯化氢通过自动催化反应加速了其他副反应，从而连续生成另外的氯化氢。此外，在氯化氢被除去的位置可以形成双键，而且若干双键会重叠而产生树脂的变色和...
【技术保护点】
1.氯乙烯聚合物的制备方法，包括以下步骤：将氯乙烯和防粘结剂置于反应器中，将反应器抽真空至压力为-0 .1～-0 .05MPa，然后通入氯气至反应器中压力为0 .2～0 .6MPa，进行氯化反应，反应结束后将反应废气排出，重复抽真空-通氯气进行氯化反应-排废气的操作，得到氯化聚氯乙烯。/n
【技术特征摘要】
1.氯乙烯聚合物的制备方法，包括以下步骤：将氯乙烯和防粘结剂置于反应器中，将反应器抽真空至压力为-0.1～-0.05MPa，然后通入氯气至反应器中压力为0.2～0.6MPa，进行氯化反应，反应结束后将反应废气排出，重复抽真空-通氯气进行氯化反应-排废气的操作，得到氯化聚氯乙烯。
2.根据权利要求1所述的制备方法，其特征在于，所述聚氯乙烯的聚合度为500～1300，含水量＜0.3wt％，粒径为100～315μm。
3.根据权利要求1所述的制备方法，其特征在于，所述防粘结剂为二氧化硅、白炭黑或滑石粉。
4.根据权利要求1或3所述的制备方法，其特征在于，所述防粘结剂的粒径为5～10μm。
5.根据权利要求1或3所述的制备方法，其特征在于，所述防粘结剂与聚氯乙烯的质量...
【专利技术属性】
技术研发人员：赵凯，王明建，卢鑫，
申请(专利权)人：安徽华塑股份有限公司，
类型：发明
国别省市：安徽;34