The invention discloses a high temperature non melting foam filling agent and a preparation method thereof. The foam filling agent is composed of polyurethane, foaming agent, refractory fiber, low temperature sintered high temperature non melting ceramic filler, stabilizer, silica, catalyst, foaming agent, halogen free flame retardant, and low melting point ceramic hot melt adhesive. Ceramic filler and refractory fiber are added to form crystal structure by low-temperature sintering and high-temperature non melting ceramic filler, so that it has fire-resistant effect after curing, so as to achieve non melting effect. Based on the implicative effect of refractory fiber, the overall fire-resistant non melting effect is more excellent.
【技术实现步骤摘要】
一种高温不融化的泡沫填充剂及其制备方法
本专利技术涉及建筑隔热材料领域，尤其是涉及一种高温不融化的泡沫填充剂。
技术介绍
聚氨酯泡沫固化后具有填缝﹑粘结﹑密封﹑隔热﹑吸音等多种效果，是一种环保节能﹑使用方便的建筑材料，可适用于密封堵漏﹑填空补缝﹑固定粘结，保温隔音，尤其适用于塑钢或铝合金门窗和墙体间的密封堵漏及防水。对应常见的聚氨酯泡沫填充剂来说，其通常加入一定量阻燃剂，但阻燃剂仅可以保证整体不燃烧，但实际上依然会出现融化滴落的情况，从而使得整体的实际效果缺失。
技术实现思路
本专利技术为克服上述情况不足，旨在提供一种能解决上述问题的技术方案。一种高温不融化的泡沫填充剂，由以下按照重量份的原料组成：聚氨酯50-80份，发泡剂20-50份，耐火纤维5-25份，低温烧结高温不熔陶瓷化填料15-20份，稳定剂0.1-2份，二氧化硅0.5-10份，催化剂3-7份，发泡助剂5-10份、无卤阻燃剂2-5份、低熔点陶瓷化热熔粘合剂2-8份。作为本专利技术进一步的方案：所述高温不融化的泡沫填充剂由...
【技术保护点】
1.一种高温不融化的泡沫填充剂，其特征在于，由以下按照重量份的原料组成：聚氨酯50-80份，发泡剂20-50份，耐火纤维5-25份，低温烧结高温不熔陶瓷化填料15-20份，稳定剂0.1-2份，二氧化硅0.5-10份，催化剂3-7份，发泡助剂5-10份、无卤阻燃剂2-5份、低熔点陶瓷化热熔粘合剂2-8份。/n
【技术特征摘要】
1.一种高温不融化的泡沫填充剂，其特征在于，由以下按照重量份的原料组成：聚氨酯50-80份，发泡剂20-50份，耐火纤维5-25份，低温烧结高温不熔陶瓷化填料15-20份，稳定剂0.1-2份，二氧化硅0.5-10份，催化剂3-7份，发泡助剂5-10份、无卤阻燃剂2-5份、低熔点陶瓷化热熔粘合剂2-8份。
2.根据权利要求1所述的高温不融化的泡沫填充剂，其特征在于，由以下按照重量份的原料组成：聚氨酯50份，发泡剂20份，耐火纤维5份，低温烧结高温不熔陶瓷化填料15份，稳定剂0.1份，二氧化硅0.5份，催化剂3份，发泡助剂5份、无卤阻燃剂2份、低熔点陶瓷化热熔粘合剂2份。
3.根据权利要求1所述的高温不融化的泡沫填充剂，其特征在于，由以下按照重量份的原料组成：聚氨酯80份，发泡剂50份，耐火纤维25份，低温烧结高温不熔陶瓷化填料20份，稳定剂2份，...
【专利技术属性】
技术研发人员：郭朝辉，
申请(专利权)人：固诺天津实业有限公司，
类型：发明
国别省市：天津;12