The invention discloses an inherently conductive polyurethane and a preparation method and application thereof. The preparation method of the invention comprises the following steps: 1) mixing the polyol and the ionic salt to make the ion dissolve in the polyol; 2) mixing the polyol dissolved in the step 1) with the polyisocyanate, the cross-linking agent and the catalyst to obtain the mixture; 3) the mixture is polymerized to cure and form the polyurethane. The polyurethane of the invention is applied to the sensor preparation. The preparation method of the invention is simple, and the raw material is cheap and easy to obtain. The polyurethane performance can be obtained through the condition adjustment control of the invention. The polyurethane is applied in the preparation of temperature and / or tension sensor.
【技术实现步骤摘要】
一种本征导电的聚氨酯及其制备方法与应用
本专利技术涉及一种本征导电的聚氨酯及其制备方法与应用，属于传感器
技术介绍
聚氨酯因其卓越的性能而被广泛应用于国民经济众多领域，为了将其应用于更广阔的领域，导电性聚氨酯、智能聚氨酯、生物可降解性聚氨酯、水凝胶聚氨酯等多功能性聚氨酯相继得到研发。现有的导电性聚氨酯一般通过共混的形式将导电物质与聚氨酯混合，如将金属纳米颗粒、碳纳米颗粒、导电高分子纳米颗粒等导电物质与聚氨酯混合均匀制备成导电的聚氨酯。这种方式制备出的聚氨酯从原理上都存在相分离的风险，即当聚氨酯多次形变时导电物质会缓慢聚集甚至从聚氨酯内部蠕动到表面，从而降低材料导的电性能与力学性能。致使聚氨酯的使用寿命大幅度缩减。聚氨酯由于其无毒能力已经广泛应用于医疗行业，但由于参杂物质的毒性使导电性的聚氨酯至今未用至医疗领域，因此，开发出生物无毒、绿色的导电类聚氨酯具有重要的意义。在生物医疗领域，高分子材料由于其生物相容性好、价格低廉、柔性可拉伸等优点占有重要的市场，但由于本身的难以导电的性能使其在传感器领...
【技术保护点】
1.一种聚氨酯的制备方法，包括如下步骤：1)将多元醇与离子盐混合，使离子溶于所述多元醇中；/n2)将步骤1)中溶解离子的多元醇与多元异氰酸酯、交联剂和催化剂混合，得到混合物；/n3)所述混合物进行聚合使其固化成型，即得到所述聚氨酯。/n
【技术特征摘要】
1.一种聚氨酯的制备方法，包括如下步骤：1)将多元醇与离子盐混合，使离子溶于所述多元醇中；
2)将步骤1)中溶解离子的多元醇与多元异氰酸酯、交联剂和催化剂混合，得到混合物；
3)所述混合物进行聚合使其固化成型，即得到所述聚氨酯。
2.根据权利要求1所述的制备方法，其特征在于：所述多元醇选自聚乙二醇、聚环氧乙烷、乙二醇、丙二醇、丁二醇、戊二醇和甘油中的至少一种；
所述离子盐选自锂盐、钠盐和钾盐中的至少一种；
所述多元异氰酸酯为二元异氰酸酯；
所述催化剂为二丁基锡二月桂酸酯。
3.根据权利要求2所述的制备方法，其特征在于：所述二元异氰酸酯包括六亚甲基二异氰酸酯、二苯基甲烷二异氰酸酯和甲苯二异氰酸酯中的至少一种；
所述交联剂包括甘油和/或聚六亚甲基二异氰酸酯。
4.根据权利要求1-3中任一项所述的制备方法，其特征在于：所述多元醇与所述离子盐的摩尔比为4～64：1；
所述多元醇与所述多元异氰酸酯的摩尔比为0.3～6：1；
所述多元醇与所述交联剂的摩尔比为0.1～10：1；
所...