The invention discloses a Longyao firewood burning ceramsite refining method, which comprises the following steps: 1) selecting the ceramsite produced in Sihui City; 2) putting the ceramsite into the mixing kettle of a high-speed mixer, adding a proper amount of water, stirring it into a paste, soaking it to get the ceramsite after aging; 3) putting the ceramsite into a vacuum mud refiner for 8-10 times, and then putting it into a pool for mud saving; 4) putting the ceramsite Seal, save 144-168h of mud. The technical scheme strictly limits the selection range of clay, and through reasonable proportion of mixing, aging and refining, it can be transformed into high-quality clay, which can withstand at least 1400 \u2103 firing, well adapt to the processing technology of Longyao firewood firing, will not have the bad situation of bursting, and ensure the perfect quality of ceramics.
【技术实现步骤摘要】
一种龙窑柴烧陶泥炼制方法
本专利技术涉及陶瓷
，特别涉及一种龙窑柴烧陶泥炼制方法。
技术介绍
中国的制瓷史已经有数千年，历代的传承与发展也使人们对陶瓷品质的要求越来越高。柴烧是一种古老的烧制方法，柴烧是指利用薪柴为燃料烧成的陶瓷制品，主要分为上釉(底釉)与不上釉(自然釉)两大类；柴烧陶器最终的烧成效果是由泥土、灰釉(落灰)、火候(温度)、窑内气氛和烧窑人的窑技等因素相互作用、相互影响，共同决定的。所以同样的陶土、在同样的温度下，在不同的窑、用不同的木材、由不同人的控制，都会烧出很多不一样的烧成效果。不同的陶土因其化学成分不同，在烧制过程中会出现的肌理、颜色效果都是不一样的，制成的陶件也会令用户产生不同的使用感受。陶土炼制成陶泥时需要考虑耐热温度、柴窑属性、薪柴种类等；追求的是让土能产生一种温润、敦厚、沉稳内敛的柴烧之美。但是现有的龙窑柴烧制作工艺，过于追求产品外观的随机性，而缺乏对部分基础工艺核心的把控，而导致制出的成品不够完美。
技术实现思路
本技术方案旨在提供一种龙窑柴烧陶泥炼制...
【技术保护点】
1.一种龙窑柴烧陶泥炼制方法，其特征在于包括以下步骤：/n1)选取四会市地区出产的陶土；/n2)将陶土放入高速混合机的搅拌釜中，添加适量的水，搅拌成浆糊状，浸泡陈腐后得到陶泥；/n3)将陶泥放入真空练泥机中进行炼制8～10遍，然后置于水池中进行省泥；/n4)将陶泥密封。/n
【技术特征摘要】
1.一种龙窑柴烧陶泥炼制方法，其特征在于包括以下步骤：
1)选取四会市地区出产的陶土；
2)将陶土放入高速混合机的搅拌釜中，添加适量的水，搅拌成浆糊状，浸泡陈腐后得到陶泥；
3)将陶泥放入真空练泥机中进行炼制8～10遍，然后置于水池中进行省泥；
4)将陶泥密封。
2.根据权利要求1所述的龙窑柴烧陶泥炼制方法，其特征在于步骤2)所添加的水量与陶土的重量比为1～2：1；优选地，所添加的水量与陶土的重量比为1：1。
3.根据权利要求1所述的龙窑柴烧陶泥炼制方法，其特征在于步骤2)所述搅拌速率为25～35r/min；优选地，所述搅拌速率为30r/min。
4...