The invention relates to a composite material for adsorbing formaldehyde and a preparation method thereof, belonging to the technical field of formaldehyde removal. The preparation method of the composite material for adsorbing formaldehyde comprises the following steps: 1) mixing n, n '\u2011 methylene bisacrylamide, acrylate, initiator and pore forming agent to obtain the mixed solution, adding the mixed solution to the polyvinyl alcohol aqueous solution for polymerization reaction, and then removing the pore forming agent with solvent washing to obtain the polymer resin; 2) mixing the polymer resin with ammonia water, and Then add the ethanol solution of tetrabutyl titanate, after reaction, solid-liquid separation, solid washing; 3) add the washed solid into HNO
【技术实现步骤摘要】
一种吸附甲醛用复合材料及其制备方法
本专利技术涉及一种吸附甲醛用复合材料及其制备方法，属于除甲醛
技术介绍
甲醛是室内大气中常见的一种污染物，它具有较高的毒性。短期接触低浓度的甲醛就会刺激眼睛及呼吸道而引起过敏反应，长期接触微量的甲醛会增加患癌的可能性。甲醛已经被世界卫生组织确定为致畸形和致癌物质。我国2003年开始实施的《室内空气质量标准》(GB/T18883-2002)规定室内空气中甲醛的最高允许浓度为0.10mg每立方米(1小时均值)。现有消除甲醛的方法有吸附法、化学吸收法、催化转化法、催化燃烧法(高低温)、光催化法、等离子体催化法等。一般在室内使用的话，不易采用较为复杂的方法，吸附法是一种最常用的消除甲醛的方法，该方法使用大比表面积的强吸附性材料吸附甲醛。但是现有的甲醛吸附材料大多采用较复杂的材料和配方，吸附甲醛的效果较差，特别是经过使用一段时间后，吸附除甲醛的效果下降，很难保证甲醛去除率。
技术实现思路
本专利技术提供一种吸附甲醛用复合材料的制备方法，以解决现有技术中甲...
【技术保护点】
1.一种吸附甲醛用复合材料的制备方法，其特征在于，包括如下步骤：/n1）将N,N'-亚甲基双丙烯酰胺、丙烯酸酯、引发剂、造孔剂混合后得混合液，然后将混合液加入聚乙烯醇水溶液中进行聚合反应，然后用溶剂洗涤除去造孔剂，得到聚合树脂；/n2）将聚合树脂与氨水混合，然后加入钛酸四丁酯的乙醇溶液，反应后，固液分离，固体洗涤；/n3）将洗涤后的固体加入HNO
【技术特征摘要】
1.一种吸附甲醛用复合材料的制备方法，其特征在于，包括如下步骤：
1）将N,N'-亚甲基双丙烯酰胺、丙烯酸酯、引发剂、造孔剂混合后得混合液，然后将混合液加入聚乙烯醇水溶液中进行聚合反应，然后用溶剂洗涤除去造孔剂，得到聚合树脂；
2）将聚合树脂与氨水混合，然后加入钛酸四丁酯的乙醇溶液，反应后，固液分离，固体洗涤；
3）将洗涤后的固体加入HNO3溶液中，恒温回流2-3h，固液分离，洗涤，干燥，即得。
2.如权利要求1所述的吸附甲醛用复合材料的制备方法，其特征在于，步骤1）中N,N'-亚甲基双丙烯酰胺、丙烯酸酯的质量比为1-3：4-10。
3.如权利要求1所述的吸附甲醛用复合材料的制备方法，其特征在于，步骤1）中所述丙烯酸酯为丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸甲酯、甲基丙烯酸乙酯中的任意一种。
4.如权利要求1所述的吸附甲醛用复合材料的制备方法，其特征在于，步骤1）中将N,N'-亚甲基双丙烯酰胺、丙烯酸酯、引发剂、造孔剂混合是...
【专利技术属性】
技术研发人员：胡鹏，张本尚，苏喜振，汤思敏，贺龙强，
申请(专利权)人：焦作大学，河南省科学院同位素研究所有限责任公司，
类型：发明
国别省市：河南;41