The invention discloses a particle grading method of archaize wall brick raw material, which is characterized in that the raw material comprises the following weight proportion: 35 \u2011 45 parts of filler, 18 \u2011 28 parts of aggregate, 35 \u2011 45 parts of plastic material, and the filler, aggregate and plastic material are at least one of clay, shale, kaolinite, montmorillonite, illite, chlorite, calcite, hematite and albite \u3002 By adjusting the particle grading of the raw materials, the maximum diameter of the aggregate is controlled within 2mm, and the rolling screen is used to vibrate the raw materials for many times, so as to control the proportion of the raw materials from the source, and then increase the adhesive force between different materials, so as to effectively avoid the deformation and deformation of the blank due to the stress concentration Crack and other problems.
【技术实现步骤摘要】
一种仿古城墙砖原料的颗粒级配方法
本专利技术涉及墙砖制造
，具体为一种仿古城墙砖原料的颗粒级配方法。
技术介绍
仿古建材中，机制城墙转由于砖的体积较大，在生产制作工艺上其技术要求很高，稍有疏忽就会造成质量问题，所以必须从原料及破碎、成型及干燥、烧结及还原等各环节工艺上，应采用特殊的制作技法。原料及破碎：原料选择和配比上，要注意骨料的合理比例和颗粒的粒径。机制砖和手工砖在原料要求上有很大区别，手工城墙砖对原料要求没有过多的要求，与其他普通砖没有大的区别，但机制城墙砖由于在成型时，采用的是挤出压力和抽取真空工艺，成型后的砖坯密实度高，这种高密度的坯体为后续的产品打下了高强度、低吸水率的基础，但也面临着坯体应力高易变形、裂纹等问题。究其原因是由于成型时采用了16％左右的成型水分，这些水分在后续的干燥脱水过程中，坯体由于水分的丢失而产生干燥收缩，当收缩产生的应力集中到砖坯的某一部位且超出砖坯本身的粘接力时，砖坯就会出现裂纹。普通砖坯由于体积较小，产生的应力较弱，而城墙砖产生的应力则较大。手工砖虽然成型水分大于机...
【技术保护点】
1.一种仿古城墙砖原料的颗粒级配方法，其特征在于，包括以下重量份数配比的原料：填充料35-45份，骨料18-28份，塑形料35-45份，所述填充料、骨料和塑形料为黏土、页岩、高岭石、蒙脱石、伊利石、绿泥石、方解石、赤铁矿和钠长石中的至少一种。/n
【技术特征摘要】
1.一种仿古城墙砖原料的颗粒级配方法，其特征在于，包括以下重量份数配比的原料：填充料35-45份，骨料18-28份，塑形料35-45份，所述填充料、骨料和塑形料为黏土、页岩、高岭石、蒙脱石、伊利石、绿泥石、方解石、赤铁矿和钠长石中的至少一种。
2.根据权利要求1所述的一种仿古城墙砖原料的颗粒级配方法，其特征在于，所述填充料、骨料和塑形料中三氧化二铁的总含量为6％-8％。
3.根据权利要求1所述的一种仿古城墙砖原料的颗粒级配方法，其特征在于，所述骨料需经破碎机破碎，破碎之后用筛子进行筛取，控制最大粒径在2mm以下。
4.根据权利要求1所述的一种仿古城墙砖原料的颗粒级配方法，其特征在于，所述填充料、骨料和塑形料中含有的化学原料有二氧化...
【专利技术属性】
技术研发人员：袁东海，谢博宣，谢祥，郭传杰，黄强，任巧雷，许运成，
申请(专利权)人：孟津青城古建制品有限公司，
类型：发明
国别省市：河南;41