The invention discloses a molding method suitable for carbon capture sodium based adsorbent, the method is that the sodium based adsorbent is soaked, dried, calcined and broken to obtain the adsorbent particles, and then the granular adsorbent particles are placed in the fluidized bed for fluidization and molding, and the required adsorbent particle size is obtained through screening; the fine powder lifted and analyzed in the collected fluidized bed is broken to the powder again, and mixed and stirred with water After mixing, drying, calcining and crushing, it is placed in the fluidized bed again for recycling. Compared with the existing sodium based adsorbent molding process, the molding method of the invention is simple and convenient, and has high production efficiency.
【技术实现步骤摘要】
一种适用于碳捕集钠基吸附剂的成型方法
本专利技术涉及一种适用于碳捕集钠基吸附剂的成型方法，属于二氧化碳减排领域。
技术介绍
随着工业化的不断发展，化石能源的过度开发利用引起了日趋严重的环境问题。由温室效应引起的温度升高等环境问题，愈发引起人们的重视。其中，由化石燃料燃烧导致空气中二氧化碳(CO2)含量的升高是温室效应的重要因素。燃煤电厂作为最大、最集中的固定单点排放源，发展适用于燃煤电厂的碳捕集技术对于缓解温室效应具有十分重要的意义。在针对电厂的各种CO2减排技术中，碱金属基吸附剂脱碳技术，由于其循环利用率高、再生能耗低、对设备腐蚀小、无二次污染等优势被认为是极具发展前景的碳捕集技术之一。美国三角研究所(RTI)、路易斯安那州立大学(LSU)和切奇杜威公司(C&D)在美国能源部(DOE)的资助下，在美国专利第6387337B1(2002.5.14)中用碱金属或碱土金属沉积在载体上，在93-1093℃下通过脱碳和再生捕集CO2。在第6280603B1(2001.08.28)中用沉淀法制备碳酸碱金属助催化...
【技术保护点】
1.一种适用于碳捕集钠基吸附剂的成型方法，其特征在于，将活性氧化铝小球粉碎后，将活性氧化铝粉末缓慢加入碳酸钠溶液浸渍搅拌，得到半干状固体进行干燥，随后煅烧；煅烧后的吸附剂块状固体进行粉碎，将吸附剂颗粒进行流化，流化后的吸附剂进行筛分，即可得到所需要的吸附剂；/n流化过程中扬析的细粉继续粉碎后，再进行与水混合搅拌，再经过干燥、煅烧、破碎、流化及筛分，得到所需要的吸附剂。/n
【技术特征摘要】
1.一种适用于碳捕集钠基吸附剂的成型方法，其特征在于，将活性氧化铝小球粉碎后，将活性氧化铝粉末缓慢加入碳酸钠溶液浸渍搅拌，得到半干状固体进行干燥，随后煅烧；煅烧后的吸附剂块状固体进行粉碎，将吸附剂颗粒进行流化，流化后的吸附剂进行筛分，即可得到所需要的吸附剂；
流化过程中扬析的细粉继续粉碎后，再进行与水混合搅拌，再经过干燥、煅烧、破碎、流化及筛分，得到所需要的吸附剂。
2.根据权利要求1所述的碳捕集钠基吸附剂的成型方法，其特征在于，所...