The invention discloses a dry papermaking method containing tea polyphenol or bacteriostatic powder. The steps are as follows: A. crushing wood pulp, open fiber and ES fiber through a crusher to obtain powder; B. adding tea polyphenol or nano silver into the powder obtained in step a to obtain mixture; C. pouring the mixture obtained in step B into the mixer to fully mix through the air flow of the pipeline; D. mixing the mixture obtained in step C The material is sprayed on the screen plate by air flow; e. the mixture on the screen plate is heated to be mutually bonded and formed; F. the formed dry paper is removed from the screen plate and then reeled. The manufacturing process is simple and convenient.
【技术实现步骤摘要】
含茶多酚或抑菌粉剂的干法造纸方法
本专利技术涉及含茶多酚或抑菌粉剂的干法造纸方法。
技术介绍
无尘纸是一种可以用于制作纸尿裤的重要材料。传统造纸需要用到水，所以造好的纸张是湿润的，必须再进行烘干处理，从而导致加工工序较多，生产较为不便。
技术实现思路
为了克服现有技术的不足，本专利技术提供生产工序简单、制作方便的干法造纸方法。本专利技术解决其技术问题所采用的技术方案是：含茶多酚或抑菌粉剂的干法造纸方法，其特征在于，步骤如下：a.将木浆、开纤、ES纤维通过破碎机打碎得到粉末;b.在a步骤中得到的粉末中加入茶多酚或纳米银得到混合料;c.将步骤b中得到的混合料倒入混合机中，通过管道气流进行充分的混合;d.将步骤c中得到的混合料通过气流喷涂到网板上;e.对网板进行加热使网板上的混合料受热相互粘合成型;f.从网板上取下成型后的干法纸然后收卷即可。本专利技术的有益效果是：本制做方法相对较为简单合理，用空气作为纤维的载体，在成形网上形成纤维薄层，再用粘合剂粘合成纸的一种特殊的造纸方法，它与传统造纸方法不同之处在于纤维是在无水情况下形成纸幅。成型后的纸张可以直接使用，无需要像传统纸张需要做烘干处理，另外在生产过程中加入了茶多酚或纳米银、纳米锌、壳聚糖等抑菌抗菌原料，从而使纸张更干净卫生。具体实施方式含茶多酚或抑菌粉剂的干法造纸方法，其特征在于，步骤如下：a.将木浆、开纤、ES纤维通过破碎机打碎得到粉末;b.在a步骤中得到的粉末中加入茶多酚或纳米银得到混合料;c.将步...
【技术保护点】
1.含茶多酚或抑菌粉剂的干法造纸方法，其特征在于，步骤如下：a.将木浆、开纤、ES纤维通过破碎机打碎得到粉末;b.在a步骤中得到的粉末中加入茶多酚或纳米银得到混合料;c. 将步骤b中得到的混合料倒入混合机中，通过管道气流进行充分的混合;d.将步骤c中得到的混合料通过气流喷涂到网板上;e.对网板进行加热使网板上的混合料受热相互粘合成型;f.从网板上取下成型后的干法纸然后收卷即可。/n
【技术特征摘要】
1.含茶多酚或抑菌粉剂的干法造纸方法，其特征在于，步骤如下：a.将木浆、开纤、ES纤维通过破碎机打碎得到粉末;b.在a步骤中得到的粉末中加入茶多酚或纳米银得到混合料;c.将步骤b中得到的混...