The invention relates to a replacement method for reducing the cadmium content in the cadmium poor solution, belonging to the technical field of zinc hydrometallurgy; a method for reducing the cadmium content in the cadmium poor solution and ensuring the one-time molding rate of sponge cadmium pressed cake, wherein the cadmium rich solution displaces the pressed cake once, the liquid displaces the pressed cake twice after the first replacement, and the liquid displaces the residual cadmium three times after the second replacement and leaches the copper cadmium residue. The invention has the advantages of ensuring the first forming rate of sponge cadmium pressed cake on the premise that the cadmium content in the cadmium poor solution is less than or equal to 100mg / L, simple principle, low cost and easy implementation, realizing the cadmium content in the cadmium poor solution is less than or equal to 100mg / L and greatly improving the output of the cadmium cake.
【技术实现步骤摘要】
一种降低贫镉液含镉的置换方法
本专利技术属于湿法炼锌领域。涉及一种降低贫镉液含镉的置换方法同时确保海绵镉压饼一次成型率的方法。
技术介绍
目前，贫镉液含镉的置换过程中存在如下问题：一次置换锌粉加入过量，海绵镉压饼不成型，要装袋返流程重新置换，成本增高；一次置换锌粉加入量不够，导致一次置换后液含镉高，增加二次置换锌粉投入，且二次置换的海绵镉无压饼条件，只能返流程重新浸出；返流程过程中二次置换桶内因海绵镉量大，容易堵塞输送泵和输送管道；因此，二次置换一次压饼工艺很难实现贫镉液含镉≤100mg/l。
技术实现思路
为了克服
技术介绍
中存在的问题，本专利技术采用新型置换方法降低贫镉液含镉。本专利技术另一个目的是解决贫镉液含镉高的问题而专利技术的一种置换方式。为了实现上述目标，本专利技术的技术方案是：一种新型降低贫镉液含镉的置换方法，由富镉液一次置换压饼、一次置换后液二次置换压饼，二次置换后液三次置换除残镉返铜镉渣浸出。其特征是在降低贫镉液含镉≤100mg/l的同时保证海绵镉压饼一次成型率。<...
【技术保护点】
1.一种新型降低贫镉液含镉的置换方法，由富镉液一次置换压饼、一次置换后液二次置换压饼，二次置换后液三次置换除残镉返铜镉渣浸出。/n
【技术特征摘要】
1.一种新型降低贫镉液含镉的置换方法，由富镉液一次置换压饼、一次置换后液二次置换压饼，二次置换后液三次置换除残镉返铜镉渣浸出。
2.根据权利要求1所述的一种新型降低贫镉液含镉的置换方法，其特征在于：其特征是在降低贫镉液含镉≤100mg/l的同时保证海绵镉压饼一次成型率。
3.根据权利要求1所述的一种新型降低贫镉液含镉的置换方法，其特征在于：针对高含镉富镉液分析误差较大时，一次置换锌粉加入量按分析富镉液含镉量的30％-40％加入，后液泵...
【专利技术属性】
技术研发人员：刘贤，张朝波，蒋勇才，郝二丽，强振华，刘福坤，段林波，保艳林，许艳芬，李芮，郭建雄，
申请(专利权)人：云南驰宏资源综合利用有限公司，
类型：发明
国别省市：云南;53