一种制备一系列高稳定性非晶双金属硅酸盐的方法技术

本发明专利技术公开了一种制备一系列高稳定性非晶双金属硅酸盐的方法，包括以硅酸钠和硫酸钴、硝酸铁、硫酸铜、硫酸铈、氯化锰为原料，室温下制备得到一类非晶双金属硅酸盐的步骤。本发明专利技术的非晶双金属硅酸盐的制备方法，反应时间短，反应温度低，工艺简单，生产效率高，适于大量生产。制备的高稳定性非晶双金属硅酸盐材料，其纯度高，稳定性高。在能源、催化、环境等领域具有广泛的应用前景。

A method of preparing a series of high stability amorphous bimetallic silicates

The invention discloses a method for preparing a series of high stability amorphous bimetallic silicates, including the steps of preparing a class of amorphous bimetallic silicates at room temperature with sodium silicate, cobalt sulfate, iron nitrate, copper sulfate, cerium sulfate and manganese chloride as raw materials. The preparation method of the amorphous bimetallic silicate has the advantages of short reaction time, low reaction temperature, simple process, high production efficiency and is suitable for mass production. The prepared amorphous bimetallic silicate material has high purity and stability. It has a wide application prospect in energy, catalysis, environment and other fields.

【技术实现步骤摘要】
一种制备一系列高稳定性非晶双金属硅酸盐的方法
本专利技术提供一种制备一系列高稳定性非晶双金属硅酸盐的方法，属于无机材料制备

技术介绍
非晶材料具有小区间范围内原子键合规律性、较宽成分范围内宏观特性可调控、均匀各向同性等特点，表现出一些特殊的理化性质，如机械柔韧性高、比表面积大、活性位点丰富、高催化活性等，已广泛应用于催化、生物、电化学储能等诸多领域，如光/电催化剂、光电器件、锂电池、功能材料等。但是目前非晶材料的制备过程复杂，周期长、纯度低。因此如何以低成本、简单高效的方法大量制备非晶材料是目前面临的一个挑战。金属硅酸盐材料在自然界中储量丰富，环境友好，化学性质稳定，且工业化应用广泛，如硅酸铁作为吸附剂从废水中选择性吸附阳离子染料；硅酸锰作为T1模式造影剂，提高核磁共振成像质量；硅酸铜作为催化剂用于加氢反应等。然而现有技术中还未有关于制备一系列高稳定性非晶双金属硅酸盐的报道。为了利用非晶材料和硅酸盐材料优异的理化性能，本专利技术提供了一种通用的高效制备高稳定性非晶双金属硅酸盐材料的方法，对于硅酸盐材料的进一步应用具有重本文档来自技高网...

【技术保护点】
1.一种制备一系列高稳定性非晶双金属硅酸盐的方法，其特征在于，包括以硅酸钠和硫酸钴、硝酸铁、硫酸铜、硫酸铈、氯化锰为原料，室温下，将硅酸钠和上述任意两种金属盐分别溶于去离子水，在搅拌作用下，将硅酸钠溶液缓慢加入到金属盐溶液中，形成混合溶液，保持15分钟，离心、洗涤产物，烘干，即得非晶双金属硅酸盐粉体。/n

【技术特征摘要】
1.一种制备一系列高稳定性非晶双金属硅酸盐的方法，其特征在于，包括以硅酸钠和硫酸钴、硝酸铁、硫酸铜、硫酸铈、氯化锰为原料，室温下，将硅酸钠和上述任意两种金属盐分别溶于去离子水，在搅拌作用下，将硅酸钠溶液缓慢加入到金属盐溶液中，形成混合溶液，保持15分钟，离心、洗涤...

【专利技术属性】
技术研发人员：李晓伟，温广武，路洪，高成昊，
申请(专利权)人：山东理工大学，
类型：发明
国别省市：山东;37