The invention relates to a method for removing the oxygen-containing functional group of super capacitor activated carbon, belonging to the technical field of super capacitor activated carbon preparation, which solves the technical problem of poor circulation stability of super capacitor activated carbon due to high oxygen content. The solution is: put the super capacitor activated carbon into a fluidized bed equipment which is heated to 180 \u2103 - 320 \u2103 in advance, and pass a certain proportion of nitrogen hydrogen mixture gas Body. At the temperature of 180 \u2103 - 320 \u2103, the activated carbon reacts with hydrogen in full and uniform contact, and the material is collected after 10min \u2011 30min. The process can effectively remove the oxygen-containing functional groups of activated carbon, has good economy and adaptability, and is suitable for industrial production.
【技术实现步骤摘要】
一种脱除超级电容活性炭含氧官能团的方法
本专利技术属于超级电容活性炭制备
，具体涉及的是一种脱除超级电容活性炭含氧官能团的方法。
技术介绍
超级电容器是通过电极与电解质之间形成的界面双层来存储能量的新型元器件。其电极材料主要为多孔碳材料，包括活性炭粉，活性炭纤维，碳纳米管和炭凝胶等，其中超级电容活性炭就是其中的佼佼者，但是超级电容活性炭表面的含氧官能团具有较强的电化学活性，在充放电时易发生分解反应，从而导致超级电容器的循坏稳定性下降，所以脱除超级电容活性炭表面含氧官能团具有重大科学和应用价值。目前，脱氧钝化的工艺主要是引入还原剂或进行高温热还原。如张在忠（公开号：CN106082210A）等将原料投入还原炉中，通过还原炉升温至650-1200℃，高温通入保护气体，静态烧制，还原1-6h。该方法有如下缺点：通过高温热还原，耗能增加，成本相应增加；还原时间长，效率低；静态烧制，热量渗透不均匀，还原不均匀；温度太高容易造成孔的塌缩，比表面积减少。如杜丕一（公开号CN109592681A）等将活性炭样品在还原气氛下，在...
【技术保护点】
1.一种脱除超级电容活性炭含氧官能团的方法，其特征在于包括以下步骤：/nS1、将流化床升温至180℃-320℃，然后向流化床的床层上加入超级电容活性炭；/nS2、保持流化床的温度不变，从流化床的进料口向流化床内通入氮氢混合气，反应10-30min，脱除超级电容活性炭的含氧官能团；/nS3、待步骤S2反应结束后，流化床自然降温至室温，然后向炉内通氮气或氩气，将步骤S2制得的超级电容活性炭通过流化床的出料口吹出并收集。/n
【技术特征摘要】
1.一种脱除超级电容活性炭含氧官能团的方法，其特征在于包括以下步骤：
S1、将流化床升温至180℃-320℃，然后向流化床的床层上加入超级电容活性炭；
S2、保持流化床的温度不变，从流化床的进料口向流化床内通入氮氢混合气，反应10-30min，脱除超级电容活性炭的含氧官能团；
S3、待步骤S2反应结束后，流化床自然降温至室温，然后向炉内通氮气或氩气，将步骤S2制得的超级电容活性炭通过流化床的出料口吹出并收集。
2.根据权利要求1所述的一种脱除超级电容活性炭含氧官能团的方法，其特征在于：在所述步骤S1中，...
【专利技术属性】
技术研发人员：陈成猛，孙国华，姚锦龙，孔庆强，朱庆华，马帅，石久龙，朱华，宋林刚，张超，
申请(专利权)人：中国科学院山西煤炭化学研究所，山西美锦能源股份有限公司，
类型：发明
国别省市：山西;14
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。