A shell material includes a shell body, a dye layer and a metal oxide layer, the dye layer is arranged on the shell body, the metal oxide layer is arranged on the dye layer, and the metal oxide layer comprises silver oxide and copper oxide. The preparation method of the shell material includes: placing the shell body in the dye solution to form a dye layer, obtaining a dye shell, wherein the dye solution contains acid dye, acid and the first solvent; and placing the dye shell in the reaction solution to form a metal oxide layer, wherein the reaction solution contains inorganic silver salt, inorganic copper salt, ammonia water and the second solvent. A shell button is made of the shell material or the shell material prepared by the preparation method of the shell material.
【技术实现步骤摘要】
贝壳材料及其制备方法和贝壳纽扣
本专利技术涉及染色
，特别是涉及贝壳材料及其制备方法和贝壳纽扣。
技术介绍
钮扣按材料分主要有树脂钮、贝壳钮、果实钮、奶酪蛋白钮、金属钮等。其中，贝壳钮来源于天然的贝壳，质感高雅，广受高端消费市场所青睐。由于贝壳的主要成分是碳酸钙，贝壳的染色有别于其它材质的钮扣。贝壳的染色主要是采用酸性染料或阳离子染料。酸性染料染贝壳的工艺，通过合适的酸性染料及助染剂对贝壳进行染色，染色效率高，成本低，但存在着染色牢度较差的问题，特别是染烟灰色的钮扣，除了色牢度差，贝壳表面的天然炫彩也会变差。
技术实现思路
基于此，有必要针对传统的贝壳染色方法色牢固差并且贝壳天然炫彩因着色层而变差的问题，提供一种贝壳材料及其制备方法和贝壳纽扣。一种贝壳材料，包括贝壳本体、染料层和金属氧化物层，所述染料层设于所述贝壳本体上，所述金属氧化物层设置在所述染料层上，所述金属氧化物层包含氧化银和氧化铜。在其中一个实施例中，所述染料层的厚度为5nm至20nm，所述金属氧化物层的厚度为5n
【技术保护点】
1.一种贝壳材料，其特征在于，包括贝壳本体、染料层和金属氧化物层，所述染料层设于所述贝壳本体上，所述金属氧化物层设置在所述染料层上，所述金属氧化物层包含氧化银和氧化铜。/n
【技术特征摘要】
1.一种贝壳材料，其特征在于，包括贝壳本体、染料层和金属氧化物层，所述染料层设于所述贝壳本体上，所述金属氧化物层设置在所述染料层上，所述金属氧化物层包含氧化银和氧化铜。
2.根据权利要求1所述的贝壳材料，其特征在于，所述染料层的厚度为5nm至20nm，所述金属氧化物层的厚度为5nm至20nm。
3.根据权利要求1或2所述的贝壳材料，其特征在于，所述金属氧化层中的氧化银和氧化铜的物质的量之比为1:(8～12)。
4.一种贝壳材料的制备方法，包括：
将贝壳本体置于染液中浸染形成染料层，得到染色贝壳，所述染液中含有酸性染料、酸和第一溶剂；以及
将所述染色贝壳置于反应液中反应形成金属氧化物层，所述反应液中含有无机银盐、无机铜盐、氨水和第二溶剂。
5.根据权利要求4所述的贝壳材料的制备方法，其特征在于，所述无机银盐为硝酸银，所述无机铜盐为硫酸铜。
6.根据权利要求4或5所述的贝壳材料的制备方法，其特征在于，在所述染液中，所述酸性染料的浓度为0.01g/L至10g/L，所述酸的浓度为0.1ml/L至0.8ml/L；和/或，
在所述反应液中，所述无机银盐的浓度为6g/L至...
【专利技术属性】
技术研发人员：何陈，王国忠，盛峭敏，
申请(专利权)人：广东溢达纺织有限公司，
类型：发明
国别省市：广东;44