The modified method of coal ash containing unburned carbon of the invention is characterized in that: receiving process, determining the L value and b value in the lab surface color system of coal ash containing unburned carbon, and selecting the coal ash containing unburned carbon with the L value of more than 54 and the b value of more than 2 and less than 10; and grading process, for the coal ash containing unburned carbon screened out in the receiving process, and The 45 \u03bc m sieve residue of the modified coal ash modified by classification is classified under the condition of 8% mass.
【技术实现步骤摘要】
【国外来华专利技术】含未燃烧碳的煤灰的改性方法、含未燃烧碳的煤灰的改性系统及混凝土外加剂用粉煤灰的制造方法
本专利技术涉及一种含未燃烧碳的煤灰的改性方法、含未燃烧碳的煤灰的改性系统及混凝土外加剂用粉煤灰的制造方法。本申请主张基于2017年3月31日于日本申请的专利申请2017-073123号的优先权，并将其内容援用于此。
技术介绍
正在研究将在燃煤火力发电厂、流化床燃烧炉等中产生的煤灰(还称为粉煤灰)用作混凝土的外加剂。混凝土外加剂用粉煤灰在日本工业标准的JISA6201(混凝土用粉煤灰)中被规定。然而，煤灰通常包含未燃烧碳，该未燃烧碳有时吸附AE剂(引气剂)、AE减水剂、减水剂等化学外加剂的成分。因此，若添加到混凝土中的煤灰的未燃烧碳量较多，则有时需要增加AE剂、AE减水剂、减水剂等化学外加剂的添加量。并且，若将未燃烧碳量多的煤灰添加到混凝土中，则有时混凝土的空气量、流动性发生变动、或者进而在所固化的混凝土的表面产生由未燃烧碳引起的黑色斑点而使外观变差。因此，正在研究用于去除含未燃烧碳的煤灰中的未燃烧碳的方法。例如，在...
【技术保护点】
1.一种含未燃烧碳的煤灰的改性方法，其特征在于，具有：/n接收工序，测定含未燃烧碳的煤灰的Lab表色系中的L值和b值，并筛选所述L值为54以上并且所述b值为2以上且10以下的含未燃烧碳的煤灰；及/n分级工序，对在所述接收工序中筛选出的所述含未燃烧碳的煤灰，以通过分级而改性的改性煤灰的45μm筛余物成为8质量％以下的条件进行分级。/n
【技术特征摘要】
【国外来华专利技术】20170331 JP 2017-0731231.一种含未燃烧碳的煤灰的改性方法，其特征在于，具有：
接收工序，测定含未燃烧碳的煤灰的Lab表色系中的L值和b值，并筛选所述L值为54以上并且所述b值为2以上且10以下的含未燃烧碳的煤灰；及
分级工序，对在所述接收工序中筛选出的所述含未燃烧碳的煤灰，以通过分级而改性的改性煤灰的45μm筛余物成为8质量％以下的条件进行分级。
2.根据权利要求1所述的含未燃烧碳的煤灰的改性方法，其特征在于，
所述含未燃烧碳的煤灰为在燃煤火力发电厂中产生的含未燃烧碳的煤灰。
3.根据权利要求1或2所述的含未燃烧碳的煤灰的改性方法，其特征在于，
在所述分级工序中，对所述含未燃烧...