The invention discloses a multifunctional printing pretreatment slurry, which comprises the following components by weight percentage: water soluble polyester 0.5-4.99%; printing paste 0.5-25%; water absorbent 1.5-20%; water 50.01-97.5%; wherein, the pH value of the multifunctional printing pretreatment slurry is 2-6 or 8-12. The invention also discloses a preparation method and application of a multifunctional printing pretreatment slurry, belonging to the field of textile printing and dyeing. The size and method of the invention solve the problems of environmental pollution caused by too large solid content in the stiff finishing of fabric before printing in the prior art and the poor effect of single-sided printing in the prior art, and provide new ideas and methods for the development of new printing products and new processes due to the excellent thermoplasticity of water-soluble polyester.
【技术实现步骤摘要】
一种印花多功能前处理浆料及其制备方法与应用
本专利技术属于纺织品印染领域，具体涉及的是一种印花多功能前处理浆料及其制备方法与应用。
技术介绍
纺织品品种众多，很多轻薄纺织品容易变形，尺寸稳定性差，印花加工难度很大，为了改善尺寸稳定性，便于印花操作，在实际应用中，轻薄面料一般通过上一层印花浆料，使面料变硬，保证尺寸稳定性。而现有印花浆料多为天然糊料或者改性天然糊料，亲水性大，上浆效果差，往往需要达到10％以上的固含量才能达到稳定尺寸的作用。并且天然糊料的分子结构中含有大量亲水基团，在放置过程中极易回潮变软，特别是空气相对湿度对上浆面料硬挺度影响很大，晴天和雨天上浆面料的硬挺度完全不一样，影响印花品质；固含量高，必须达到10％以上固含量，有时为了增加硬挺度，使用糊精做上浆硬挺剂，含量甚至超过50％，印花结束后，这些糊料都要通过水洗去除，大大增加了废水的COD排放指标，造成严重污染；另外，在纺织品印花中，为了造成差异化产品，很多印花品种要求单面印花，反面不能有任何渗透痕迹，而现有技术使用常规印花糊料配成浆料，上浆烘干后再印...
【技术保护点】
1.一种印花多功能前处理浆料，其特征在于，它包括如下重量百分比的组分：/n
【技术特征摘要】
1.一种印花多功能前处理浆料，其特征在于，它包括如下重量百分比的组分：
其中，所述印花多功能前处理浆料的pH值为2～6或8～12。
2.根据权利要求1所述的印花多功能前处理浆料，其特征在于，所述的印花糊料为天然糊料、改性糊料和合成糊料中的任意一种或几种组合。
3.根据权利要求2所述的印花多功能前处理浆料，其特征在于，所述的天然糊料为海藻酸钠、淀粉、汉生胶和龙胶中的任意一种或几种组合；
其中，所述的淀粉为未改性淀粉和酸水解淀粉中的任意一种或两种组合。
4.根据权利要求2所述的印花多功能前处理浆料，其特征在于，所述的改性糊料为淀粉醚类、纤维素醚类、种子胶醚类中的任意一种或几种组合。
5.根据权利要求2所述的印花多功能前处理浆料，其特征在于，所述的合成糊料为聚丙烯类增稠剂、聚氨酯类增稠剂和无机矿物增稠剂中的任意一种或几种组合。
6.根据权利要求1所述...