一种甘草药渣基分级多孔炭及其制备方法和应用技术

本发明专利技术涉及炭材料技术领域，尤其涉及一种甘草药渣基分级多孔炭及其制备方法和应用。本发明专利技术提供的所述制备方法步骤简单，适于工业化生产；以甘草药渣为前驱体，实现了资源的再利用；同时，所述制备方法制备得到的甘草药渣基分级多孔炭比表面积高、孔径分布合理，其作为电极材料时能量密度高。

A kind of graded porous carbon based on licorice residue and its preparation and Application

The invention relates to the technical field of carbon materials, in particular to a Glycyrrhiza residue based graded porous carbon and a preparation method and application thereof. The preparation method provided by the invention has simple steps and is suitable for industrial production; taking licorice residue as the precursor, the resource reuse is realized; at the same time, the licorice residue based graded porous carbon prepared by the preparation method has high specific surface area, reasonable pore size distribution and high energy density when it is used as electrode material.

【技术实现步骤摘要】
一种甘草药渣基分级多孔炭及其制备方法和应用
本专利技术涉及炭材料
，尤其涉及一种甘草药渣基分级多孔炭及其制备方法和应用。
技术介绍
随着全球人口的快速增长以及对化石能源的过渡依赖，人类面临日益严重的能源危机和环境问题，这促使人们开发清洁、高效、可再生的新能源以及探索新能源的存储与转换技术。超级电容器，主要由电极、隔膜、电解液、集流器组成，是建立在双电层理论基础上的一种全新电容器。其中，超级电容器的电极材料作为储能设备的主要组成部分，对储能设备的电化学性能起着决定性的作用。生物质作为含量比较丰富的可再生资源，是人类将来生存发展的一种重要能源，将生物质在高温下进行脱氢脱氧处理制备得到炭材料是生物质利用的一种有效途径。现有技术中以生物质作为碳源制备炭材料已经得到了人们的广泛关注，相关研究者使用各种方式制备炭材料，例如：化学活化法、模板法或CO2活化法等。但是上述方案存在着以下缺点：对前驱体的预处理比较繁琐，无法适应于工业化生产，制备得到的炭材料比表面积低，孔径分布不合理，导致其作为电极材料时，能量密度低。目前，中草药加工产业中依本文档来自技高网...

【技术保护点】
1.一种甘草药渣基分级多孔炭的制备方法，其特征在于，包括以下步骤：/n将甘草药渣进行第一热处理，得到预炭化产物；/n将所述预炭化产物和碱液混合后干燥，进行第二热处理，得到甘草药渣基分级多孔炭。/n

【技术特征摘要】
1.一种甘草药渣基分级多孔炭的制备方法，其特征在于，包括以下步骤：
将甘草药渣进行第一热处理，得到预炭化产物；
将所述预炭化产物和碱液混合后干燥，进行第二热处理，得到甘草药渣基分级多孔炭。


2.如权利要求1所述的制备方法，其特征在于，进行所述第一热处理前，对所述甘草药渣进行预处理；
所述预处理包括洗涤和干燥。


3.如权利要求1所述的制备方法，其特征在于，所述第一热处理在N2气氛中进行；
所述第一热处理的温度为300～400℃，所述第一热处理的保温时间为50～70min。


4.如权利要求3所述的制备方法，其特征在于，升温至所述第一热处理温度的升温速率为4～6℃/min。


5.如权利要求1所述的制备方法，其特征在于，所述碱液为氢氧化钾水溶液；
所述碱液的浓度为0.7～2mo...

【专利技术属性】
技术研发人员：张根林，陈利威，周倩云，党艳艳，
申请(专利权)人：石河子大学，
类型：发明
国别省市：新疆;65