The invention relates to a process for removing impurity elements in electrolytic metal chromium, belonging to the technical field of element purification. After heating, the electrolytic metal chromium is crushed and pressed into cake to obtain the chromium powder after impurity removal; or the electrolytic metal chromium is crushed and added with carbon element powder / tin element powder and pressed into cake to obtain the chromium powder after impurity removal. The invention can be heated in vacuum state in a certain time and under certain conditions, and the content of O can be reduced to less than 300ppm, the content of S can be reduced to less than 10ppm, and the content of N can be reduced to less than 20ppm.
【技术实现步骤摘要】
去除电解金属铬中杂质元素的工艺
本专利技术涉及一种去除电解金属铬中杂质元素的工艺，该工艺能够去除氧元素、硫元素或氮元素，属于元素提纯
技术介绍
镍、钴高温合金是一种成分非常复杂的多组元合金，一般都含有强氧化物形成元素，如Ti、Al；此外，Cr作为一种必不可少的合金化元素，其原材料中含有大量的氧，所以，在上述元素含量较高的合金熔炼过程中，O一直无法得到有效地去除。当镍、钴基高温合金的O元素含量较高时，很容易形成氧化物，这些氧化物夹杂数量过多时，就会在合金服役过程中形成裂纹源，进一步成为裂纹产生和扩展的通道，从而降低合金的疲劳和蠕变性能，因此，必须严格控制合金中O元素的含量。真空加热提纯是一种在真空条件下利用硅碳棒加热原理来促使氧、碳反生化学反应的工艺。高合金化优质高温合金需要选用含氧量低的金属铬。随着高温合金的不断发展，对合金中的气体含量及夹杂物含量都提出了越来越高的要求。目前，国外较为成熟的真空感应熔炼可以将合金中的O含量降到10ppm以下，然而国内同样采用真空感应熔炼，却因为金属铬含氧量达到1000-20...
【技术保护点】
1.去除电解金属铬中杂质元素的工艺，其特征是：将电解金属铬粉碎压饼，加热后即得到除杂后的铬粉；或将电解金属铬粉碎后添加碳元素粉末/锡元素粉末压饼加热后即得到除杂后的铬粉。/n
【技术特征摘要】
1.去除电解金属铬中杂质元素的工艺，其特征是：将电解金属铬粉碎压饼，加热后即得到除杂后的铬粉；或将电解金属铬粉碎后添加碳元素粉末/锡元素粉末压饼加热后即得到除杂后的铬粉。
2.如权利要求1所述去除电解金属铬中杂质元素的工艺，其特征是：所述杂质元素具体为氧元素、硫元素或氮元素。
3.去除电解金属铬中氧元素的工艺，其特征是步骤如下：
（1）粉碎：将电解金属铬通过振动粉碎机进行粉碎，得到铬粉，测定铬粉末中的氧含量，待用；
（2）压饼：在步骤（1）所得铬粉中加入碳元素粉末，通过搅拌机充分混合，用冲压机压制成圆饼，待用；
（3）加热：将步骤（2）所得圆饼放入真空烧结炉中进行加热，通过发生氧、碳化学反应，形成气体碳氧化合物，并经真空泵抽出。
4.如权利要求3所述去除电解金属铬中氧元素的工艺，其特征是：
步骤（2）中，加入碳元素粉末的重量按照铬粉的含氧量计，碳元素粉末重量为每公斤铬粉含氧量的1%-2%；步骤（2）中碳元素粉末的目数为80-120目；
步骤（3）中真空烧结炉中的真空度为3-15Pa，加热至900-1150℃，加热30-48小时。
5.去除电解金属铬中氮元素的工艺，其特征是步骤如下：
（1）粉碎：将电解金属铬通过振动粉碎机进行粉碎，得到铬粉；
（2）压制：将步骤（1）所得铬粉用冲压机压制成圆饼，待用；
（3）真空加热：将步...